Effect of curing temperature on the behaviour of UHPFRC at elevated temperatures

被引：48

作者：

Kahanji, Charles ^{[1
]}

Ali, Faris ^{[2
]}

Nadjai, Ali ^{[2
]}

Alam, Naveed ^{[2
]}

机构：

[1] Stellenbosch Univ, Dept Civil Engn, ZA-7602 Stellenbosch, South Africa

[2] Ulster Univ, Sch Built Environm, Built Environm Res Inst, FireSERT, Shore Rd, Newtownabbey BT37 0QB, North Ireland

来源：

CONSTRUCTION AND BUILDING MATERIALS | 2018年 / 182卷

关键词：

Ultra-high performance fibre reinforced concrete; ISO; 834; Fire resistance; Concrete beams; Steel fibres; Polypropylene fibres; Spalling; Curing; Residual strength; HIGH-PERFORMANCE CONCRETE; MECHANICAL-PROPERTIES; RESIDUAL STRENGTH; EXPOSURE; REGIME; FIBERS;

D O I：

10.1016/j.conbuildmat.2018.06.163

中图分类号：

TU [建筑科学];

学科分类号：

0813 ;

摘要：

Ultra-high performance fibre reinforced concrete is one of the construction materials that is still in need of more research to evaluate its performance under fire, particularly regarding explosive spalling. In this study, the effect of curing temperature on the fire resilience of ultra-high performance fibre reinforced concrete (UHPFRC) has been tested. In particular, the influence of cold (20 degrees C) and hot (90 degrees C) water curing temperatures on the performance of UHPFRC exposed to elevated temperatures has been investigated. Beams, cured in cold water and in hot water were tested under the standard ISO 834 heating regime. The test results showed that the beam cured in hot water spalled significantly more than the beam cured in cold water. The study further investigated the influence of curing temperature on the residual strength of UHPFRC (containing both steel and polypropylene fibres). The cube elements were heated at eight selected temperatures between 200 degrees C and 900 degrees C. The cold-cured concrete exhibited higher relative residual strength at all temperatures. The results further showed that UHPFRC have high strength retention up to 600 degrees C. The residual peak strength for both the cold and the hot-cured occurred at 400 degrees C. (C) 2018 Elsevier Ltd. All rights reserved.

引用

页码：670 / 681

页数：12

共 33 条

[1]

Ahlborn T. M., 2008, P 2 INT S ULTR PERF, P197

[2]

[Anonymous], FIR RES TESTS EL B 1

[3]

B. S. Institution, 2012, 136312012 BS EN

[4]

Behloul M., 2002, 1 FIB C, P421

[5] Residual strength of hybrid-fiber-reinforced high-strength concrete after exposure to high temperatures [J].

Bing, C ;

Liu, JY .

CEMENT AND CONCRETE RESEARCH, 2004, 34 (06) :1065-1069

[6]

Burke B T., 2011, Residual Strength of Ultra-High Performance Concrete after Exposure to Elevated Temperature" Master's Degree Thesis, University of Connecticut

[7] Residual strength and pore structure of high-strength concrete and normal strength concrete after exposure to high temperatures [J].

Chan, YN ;

Peng, GF ;

Anson, M .

CEMENT & CONCRETE COMPOSITES, 1999, 21 (01) :23-27

[8] MICROSTRUCTURAL ANALYSIS OF RPC (REACTIVE POWDER CONCRETE) [J].

CHEYREZY, M ;

MARET, V ;

FROUIN, L .

CEMENT AND CONCRETE RESEARCH, 1995, 25 (07) :1491-1500

[9]

Comeau E. D., 1997, NFPA J, V91, P58

[10]

Graybeal BA., 2007, Material Property Characterization of Ultra-High Performance Concrete

← 1 2 3 4 →