Notched fatigue of Zr-based bulk metallic glass

被引:3
作者
Nakai, Yoshikazu [1 ]
Sei, Naoki [2 ]
Kim, Bok-Key [3 ]
机构
[1] Kobe Univ, Dept Mech Engn, Kobe, Hyogo 6578501, Japan
[2] Kobe Univ, Grad Sch Sci & Technol, Kobe, Hyogo 6578501, Japan
[3] Myongji Coll, Mech Design Sect, Seoul 120776, South Korea
来源
MECHANICAL BEHAVIOR OF MATERIALS X, PTS 1AND 2 | 2007年 / 345-346卷
关键词
notched fatigue; Zr-based bulk metallic glass; fatigue crack initiation;
D O I
10.4028/www.scientific.net/KEM.345-346.259
中图分类号
T [工业技术];
学科分类号
08 ;
摘要
In the present study, fatigue tests of sharp-notched Zr-based bulk metallic glass (BGM), were conducted under fully reversed cyclic bending, and the fatigue crack initiation mechanisms were clarified by using AFM. The fracture surface was also observed to examine the crack propagation mechanism. The fatigue notch factor was 2.0, while the elastic stress concentration factor is 2.7. From the macroscopic observations of fractured specimen, either tension mode or shear mode fracture morphologies were observed. Either in smooth specimens or notched specimens, no prodigious sign of crack initiation were observed, i.e., fatigue cracks were initiated from shear bands those were formed just before the crack initiation.
引用
收藏
页码:259 / +
页数:2
相关论文
共 6 条
  • [1] Fatigue of a Zr-Ti-Cu-Ni-Be bulk amorphous metal: Stress/life and crack-growth behavior
    Gilbert, CJ
    Lippmann, JM
    Ritchie, RO
    [J]. SCRIPTA MATERIALIA, 1998, 38 (04) : 537 - 542
  • [2] NAKAI Y, 2006, P FATIGUE
  • [3] NEUBER H, 1958, KERBSPANNUNGSLEHRE, P73
  • [4] The fatigue behavior of a zirconium-based bulk metallic glass in vacuum and air
    Peter, WH
    Buchanan, RA
    Liu, CT
    Liaw, PK
    [J]. JOURNAL OF NON-CRYSTALLINE SOLIDS, 2003, 317 (1-2) : 187 - 192
  • [5] Fatigue behavior of Zr-Ti-Ni-Cu-Be bulk-metallic glasses
    Wang, GY
    Liaw, PK
    Peker, A
    Yang, B
    Benson, ML
    Yuan, W
    Peter, WH
    Huang, L
    Freels, A
    Buchanan, RA
    Liu, CT
    Brooks, CR
    [J]. INTERMETALLICS, 2005, 13 (3-4) : 429 - 435
  • [6] Fatigue behavior and fracture morphology of Zr50Al10Cu40 and Zr50Al10Cu30Ni10 bulk-metallic glasses
    Wang, GY
    Liaw, PK
    Peter, WH
    Yang, B
    Freels, M
    Yokoyama, Y
    Benson, ML
    Green, BA
    Saleh, TA
    McDaniels, RL
    Steward, RV
    Buchanan, RA
    Liu, CT
    Brooks, CR
    [J]. INTERMETALLICS, 2004, 12 (10-11) : 1219 - 1227