X-ray characterization of inert gas atomized low carbon astroloy powder

被引：1

作者：

Kumar, M ^{[1
]}

Naidu, SVN ^{[1
]}

机构：

[1] Def Met Res Lab, Hyderabad 500058, Andhra Pradesh, India

来源：

MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING | 2004年 / 385卷 / 1-2期

关键词：

X-ray diffraction; low carbon astroloy powder; dendrite arm spacings;

D O I：

10.1016/j.msea.2004.02.062

中图分类号：

TB3 [工程材料学];

学科分类号：

0805 ; 080502 ;

摘要：

X-ray studies were carried out on an inert gas atomized low carbon (LC) astroloy powder. The as-atomized powder was sieved into different fractions of narrow size using suitable combination of sieves to study the effect of particle size on the compositional homogeneity and lattice parameter. Using a slow scanning X-ray diffraction technique, the lattice parameter of the sample and broadening of the X-ray reflections were determined for different fractions. The results showed systematic variations with average particle size. The dendrite arm spacings measured by optical metallography showed a direct correlation with the average particle size. The observed broadening has been found to be due to the inhomogeneity in composition of the alloy developed during atomization. (C) 2004 Published by Elsevier B.V.

引用

页码：1 / 5

页数：5

共 11 条

[1]

CULLITY BD, 1959, ELEMENTS XRAY DIFFRA, P177

[2]

Gessinger G.H., 1974, International Metallurgical Reviews, V19, P51, DOI [10.1179/imtlr.1974.19.1.51, DOI 10.1179/IMTLR.1974.19.1.51]

[3]

GESSINGER GH, 1984, POWDER METALLURGY SU, P22

[4]

GESSNGER GH, 1974, INT METALL REV, V19, P52

[5]

JOLY PA, 1974, J MATER SCI, V9, P1450

[6] MICROSTRUCTURAL REFINEMENT OF A SUPERALLOY BY PROGRESSIVE INDUCTION MELTING [J].

KUMAR, M .

HIGH TEMPERATURE TECHNOLOGY, 1989, 7 (02) :87-90

[7]

LEMINGS MC, 1974, SOLIDIFICATION PROCE, P148

[8]

LUBANSKA H, 1970, J MET, P341

[9]

MEHROTRA SP, 1981, POWDER METALL INT, V13, P133

[10]

NAIDU SVN, 1971, METALL T, V2, P309

← 1 2 →