Preferential grain orientation in hot pressed TiB2

被引：35

作者：

Jensen, Morten Sundheim ^{[1
]}

Einarsrud, Mari-Ann ^{[1
]}

Grande, Tor ^{[1
]}

机构：

[1] Norwegian Univ Sci & Technol, Dept Mat Sci & Engn, N-7491 Trondheim, Norway

来源：

JOURNAL OF THE AMERICAN CERAMIC SOCIETY | 2007年 / 90卷 / 04期

关键词：

D O I：

10.1111/j.1551-2916.2007.01623.x

中图分类号：

TQ174 [陶瓷工业]; TB3 [工程材料学];

学科分类号：

0805 ; 080502 ;

摘要：

Preferential grain growth is reported for hot pressed titanium diboride (TiB2) prepared at 1800 degrees C and 50 MPa. Orientation imaging microscopy and X-ray diffraction revealed that the grains in the material were preferentially orientated with the [001] direction parallel to the mechanical field. The experimental findings are discussed, with emphasis on the anisotropic properties of TiB2.

引用

页码：1339 / 1341

页数：3

共 20 条

[1]

[Anonymous], [No title captured]

[2] Influence of the kinds of aluminum source on the preferential orientation and properties of Naβ-alumina ceramics [J].

Asaoka, Hiroshi ;

Ogawa, Rie ;

Hayashi, Hidetaka ;

Kishimoto, Akira .

JOURNAL OF THE CERAMIC SOCIETY OF JAPAN, 2006, 114 (1332) :719-721

[3] EFFECT OF RESIDUAL NICKEL CONTENT ON THE GRAIN-SIZE DEPENDENT MECHANICAL-PROPERTIES OF TIB2 [J].

BECHER, PF ;

FINCH, CB ;

FERBER, MK .

JOURNAL OF MATERIALS SCIENCE LETTERS, 1986, 5 (02) :195-197

[4]

BILLEHAUQ KB, 1980, ALUMINIUM, V56, P642

[5] A TEM study on TiB2-20%MoSi2 composite:: Microstructure development and densification mechanism [J].

Biswas, K ;

Basu, B ;

Suri, AK ;

Chattopadhyay, K .

SCRIPTA MATERIALIA, 2006, 54 (07) :1363-1368

[6]

BOXALL LG, 1984, LIGHT METALS 1984, P573

[7] Hot forging of a textured α-sialon ceramic [J].

Carman, A ;

Pereloma, E ;

Cheng, YB .

JOURNAL OF THE AMERICAN CERAMIC SOCIETY, 2006, 89 (02) :478-483

[8]

DORWARD RC, 1982, J AM CERAM SOC, V65, pC6, DOI 10.1111/j.1151-2916.1982.tb09927.x

[9]

FERBER MK, 1983, J AM CERAM SOC, V66, pC2, DOI 10.1111/j.1151-2916.1983.tb09974.x

[10]

Graziani T., 1992, International Journal of Refractory & Hard Metals, V11, P105, DOI 10.1016/0263-4368(92)90073-B

← 1 2 →