Effect of Precipitation Hardening Treatment on Corrosion Behavior and Anodic Efficiency of Sacrificial Anode Produced from Recycled Al-Zn-Mg Alloy

被引：6
作者：
Abubakar, Muazu [1 ]
Onimisi, Muhammed Abdulrasheed [1 ]
机构：
[1] Bayero Univ Kano, Dept Mech Engn, Kano 33100, Nigeria
来源：
JOURNAL OF FAILURE ANALYSIS AND PREVENTION | 2021年 / 21卷 / 04期
关键词：
X-ray techniques; Corrosion; MgZn2; Phase; Precipitation hardening; ALUMINUM-ALLOY; LOCALIZED CORROSION; CU ALLOY; MICROSTRUCTURE; TI; RESISTANCE; STRENGTH; CHLORIDE;
D O I：
10.1007/s11668-021-01150-6
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
In this work, Al-Zn-Mg sacrificial anode was developed from recycled aluminum and zinc. Characterization of the alloy using XRD, TEM and optical microscopy was conducted. Also, the influence of precipitation hardening time on the performance of the sacrificial anodes in seawater was investigated. The results indicated that the formation of both stable and metastable MgZn2 phase during precipitation hardening process has a significant effect on the corrosion behavior of the alloy. The high anodic efficiency of the alloy was attributed to the formation of the stable MgZn2 (eta-phase) within the aluminum matrix.
引用
收藏
页码：1212 / 1219
页数：8
相关论文
共 29 条
[11]   Microstructural evolution and aging behavior of cryorolled Al-4Zn-2Mg alloy [J].
Krishna, K. Gopala ;
Sivaprasad, K. ;
Venkateswarlu, K. ;
Kumar, K. C. Hari .
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2012, 535 :129-135
[12]   Effect of aging time on precipitation behavior, mechanical and corrosion properties of a novel Al-Zn-Mg-Sc-Zr alloy [J].
Li, Bo ;
Pan, Qing-lin ;
Chen, Cong-ping ;
Yin, Zhi-min .
TRANSACTIONS OF NONFERROUS METALS SOCIETY OF CHINA, 2016, 26 (09) :2263-2275
[13]   Investigation of the Localized Corrosion Resistance of 4044 Aluminum Alloy in Acid Chloride and Neutral Chloride Solutions [J].
Loto R.T. .
Journal of Failure Analysis and Prevention, 2018, 18 (04) :905-911
[14]   Corrosion analysis of Al-Zn-In-Mg-Ti-Mn sacrificial anode alloy [J].
Ma, Jingling ;
Wen, Jiuba .
JOURNAL OF ALLOYS AND COMPOUNDS, 2010, 496 (1-2) :110-115
[15]   Influence of Mg and Ti on the microstructure and electrochemical performance of aluminum alloy sacrificial anodes [J].
Ma Jingling ;
Wen Jiuba ;
Li Xudong ;
Zhao Shengli ;
Yan Yanfu .
RARE METALS, 2009, 28 (02) :187-192
[16]   Pitting behavior of aluminum ion implanted with nitrogen [J].
McCafferty, E ;
Natishan, PM ;
Hubler, GK .
CORROSION, 1997, 53 (07) :556-561
[17]   Sacrificial Anode Stability and Polarization Potential Variation in a Ternary Al-xZn-xMg Alloy in a Seawater-Marine Environment [J].
Muazu, Abubakar ;
Aliyu, Yaro Shehu ;
Abdulwahab, Malik ;
Popoola, Abimbola Patricia Idowu .
JOURNAL OF MARINE SCIENCE AND APPLICATION, 2016, 15 (02) :208-213
[18]   Microstructure and corrosion resistance of molybdenum and aluminum coatings thermally sprayed on 7075-T6 aluminum alloy [J].
Naimi, A. ;
Yousfi, H. ;
Trari, M. .
PROTECTION OF METALS AND PHYSICAL CHEMISTRY OF SURFACES, 2012, 48 (05) :557-562
[19]   Effect of segregation on initiation of corrosion of aluminium sacrificial anode containing mischmetal [J].
Qi, G. T. ;
Xiong, W. ;
Zhu, W. T. .
CORROSION ENGINEERING SCIENCE AND TECHNOLOGY, 2011, 46 (04) :458-463
[20]   Influence of various aging treatments on microstructure, strength and corrosion behaviour of high Zn content Al-Zn-Mg-Cu alloy [J].
Ran, F. Q. ;
Chai, L. H. ;
Gao, K. Y. ;
Nie, Z. R. ;
Chen, Z. Y. .
CORROSION ENGINEERING SCIENCE AND TECHNOLOGY, 2014, 49 (08) :712-718
123