High-energy ball milling of Cu-5mass%C powders

被引：0
作者：
Jin, YP [1 ]
Guo, B [1 ]
Wang, ED [1 ]
机构：
[1] Harbin Inst Technol, Sch Mat Sci & Engn, Harbin 150001, Peoples R China
来源：
PROCEEDINGS OF THE 1ST INTERNATIONAL CONFERENCE ON NEW FORMING TECHNOLOGY | 2004年
关键词：
ball milling; Cu-5mass%C composite powders; grain refinement; distortion of lattice;
D O I：
暂无
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
Cu-5mass%C composite powders were prepared by high-energy ball milling. Their microstructures and effects of ball milling time on their microstructure were investigated. The result shows that distortion of lattice, grain refinement and broadened diffraction peak of Cu were seen after high-energy ball milling. Within the initial 2 hours of ball milling, grain of Cu in Cu-5mass%C composite powders was refined suddenly, then slowly. Grain size of Cu was about 20nm by ball milling for 5h. Diffraction peak of graphite disappeared after 2-hour-milling. High-energy ball milling extended solid solubility of C in Cu. Microstrain of Cu in Cu-5mass%C composite powders didn't increase with milling time. After ball milling for 3h, microstrain reached the maximum value. Over 15h-ball milling hardly affected microstrain of Cu in Cu-5mass%C composite powders.
引用
收藏
页码：639 / 643
页数：5
相关论文
共 50 条
  • [41] Phase transformation of nanocrystalline anatase powders during high energy planetary ball milling
    Pan, XY
    Chen, Y
    Ma, XM
    Zhu, LH
    TRANSACTIONS OF NONFERROUS METALS SOCIETY OF CHINA, 2003, 13 (02) : 271 - 275
  • [42] Phase transformation of nanocrystalline anatase powders during high energy planetary ball milling
    潘晓燕
    陈怡
    马学鸣
    朱丽慧
    Transactions of Nonferrous Metals Society of China, 2003, (02) : 271 - 275
  • [43] Effect of high energy ball milling on the displacement reaction in particulate reinforced Al–Si–Cu alloy matrix composite powders
    H. W. Huo
    K. D. Woo
    G. S. Guo
    D. L. Zhang
    Journal of Materials Science, 2007, 42 : 59 - 65
  • [44] Evolution of Nanostructure States of Cu-powders Prepared by Ball Milling
    Boytsov, Oleg
    Ustinov, A. I.
    Gaffet, E.
    Bernard, F.
    ACTA CRYSTALLOGRAPHICA A-FOUNDATION AND ADVANCES, 2005, 61 : C449 - C450
  • [45] Thermal Stability of Carbohydrides Obtained by the High-Energy Ball Milling of Titanium in a Toluene Medium
    Aksenova, V. V.
    Kanunnikova, O. M.
    Burnyshev, I. N.
    Pushkarev, B. E.
    Ladyanov, V., I
    JOURNAL OF SURFACE INVESTIGATION, 2022, 16 (01): : 68 - 72
  • [46] Effect of jar shape on high-energy planetary ball milling efficiency: Simulations and experiments
    Broseghini, M.
    D'Incau, M.
    Gelisio, L.
    Pugno, N. M.
    Scardi, P.
    MATERIALS & DESIGN, 2016, 110 : 365 - 374
  • [47] Synthesis, sintering and characterization of PNZST ceramics from high-energy ball milling process
    Zhang, Lin
    Xu, Zhuo
    Feng, Yujun
    Hu, Yuanyuan
    Yao, Xi
    CERAMICS INTERNATIONAL, 2008, 34 (04) : 709 - 713
  • [48] Preparation of nanocrystalline CuAlFeS2-mixed chalcopyrite by high-energy ball milling
    Pradhan, S. K.
    Ghosh, B.
    Roy, S. Dutta
    Samanta, L. K.
    PHYSICA E-LOW-DIMENSIONAL SYSTEMS & NANOSTRUCTURES, 2006, 33 (01) : 66 - 68
  • [49] Thermal Stability of Carbohydrides Obtained by the High-Energy Ball Milling of Titanium in a Toluene Medium
    V. V. Aksenova
    O. M. Kanunnikova
    I. N. Burnyshev
    B. E. Pushkarev
    V. I. Ladyanov
    Journal of Surface Investigation: X-ray, Synchrotron and Neutron Techniques, 2022, 16 : 68 - 72
  • [50] High-energy ball-milling-induced non-equilibrium phase transformations
    Chen, Y
    Williams, JS
    MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 1997, 226 : 38 - 42
12345