Synthesis and luminescence of Sr2SiO4:Eu3+ micro-spherical phosphors by a spray-drying process

We synthesized Sr2SiO4:Eu3+ phosphors with spherical morphology by a spray-drying process. The obtained samples were characterized by XRD, SEM, and spectrophotometer. The XRD results show that samples have good crystallinity after the heat-treatment at 1150 degrees C. The higher temperature has no obvious influence on the crystallinity and will destroy the spherical morphology. The SEM results show that the phosphors are microspheres with size in the range of 0.8-2.1 mu m when they were heat treated at 1050 degrees C and 1150 degrees C. The excitation and emission spectra of the samples indicate that Eu3+ ions doped into Sr2SiO4 host successfully. The Sr2SiO4:Eu3+ sample heat-treated at 1150 degrees C has the highest emission intensity and the longest decay times. The results of this work indicate that the optimized heat-treatment temperature should be at 1150 degrees C for Sr2SiO4:Eu3+ micro-spherical phosphors synthesized by the spray-drying process.