Thermal stability of an Al/Ni3Al composite processed by powder metallurgy

被引:33
作者
Lieblich, M
GonzalezCarrasco, JL
Caruana, G
机构
关键词
nickel aluminides; based on Ni3Al; composites; thermal stability; phase transformations;
D O I
10.1016/S0966-9795(97)00027-7
中图分类号
O64 [物理化学(理论化学)、化学物理学];
学科分类号
070304 ; 081704 ;
摘要
The potential of Al/Ni3Al composites for high-temperature applications, especially when friction is involved, is currently being explored. In this work, the thermal stability of an Al/Ni3Al composite obtained by extrusion of Al and 5 vol% of spherical Ni3Al powder particles was investigated at temperatures up to 500 degrees C. The metal/intermetallic composite proved stable up to 300 degrees C. At higher temperatures, dissolution of Ni3Al particles occurred with formation of concentric layers of Al3Ni and Al3Ni2 phases. The amount of Ni aluminides for each annealing condition was determined by applying a specifically developed mathematical procedure. Dissolution of Ni3Al up to 500 degrees C was found to obey a parabolic-type law with an activation energy of 156 kJ mol(-1). Activation energies for growth of Al3Ni2 and Al3Ni were 209 and 110 kJ mol(-1), respectively, in agreement with the literature. The thermal stability shown by this composite makes it a good candidate for high-temperature applications up to 300 degrees C. (C) 1997 Elsevier Science Limited.
引用
收藏
页码:515 / 524
页数:10
相关论文
共 24 条
[1]   Solid state reactions and microstructural evolution of Al-Ni powders during high-energy ball milling [J].
Cardellini, F ;
Mazzone, G ;
Antisari, MV .
ACTA MATERIALIA, 1996, 44 (04) :1511-1517
[2]   SOLID-STATE REACTIONS BETWEEN NI AND AL POWDERS INDUCED BY PLASTIC-DEFORMATION [J].
CARDELLINI, F ;
MAZZONE, G ;
MONTONE, A ;
ANTISARI, MV .
ACTA METALLURGICA ET MATERIALIA, 1994, 42 (07) :2445-2451
[3]   FORMATION OF INTERMETALLIC LAYERS IN DIFFUSION COUPLES [J].
CASTLEMAN, LS ;
SEIGLE, LL .
TRANSACTIONS OF THE AMERICAN INSTITUTE OF MINING AND METALLURGICAL ENGINEERS, 1957, 209 :1173-1174
[4]  
CASTLEMAN LS, 1958, T AM I MIN MET ENG, V212, P589
[5]  
CRANK J, 1975, MATH DIFFUSION, P97
[6]   Ni3Al intermetallic particles as wear-resistant reinforcement for Al-base composites processed by powder metallurgy [J].
Diaz, C ;
GonzalezCarrasco, JL ;
Caruana, G ;
Lieblich, M .
METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 1996, 27 (10) :3259-3266
[7]   NIAL FORMATION BY ANNEALING OF INFILTRATED ALUMINUM-NICKEL PRECURSORS [J].
DUNAND, DC .
JOURNAL OF MATERIALS SCIENCE, 1994, 29 (15) :4056-4060
[8]   REACTION-KINETICS AND BIASING IN AL/NI MULTILAYERS [J].
EDELSTEIN, AS ;
EVERETT, RK ;
RICHARDSON, GR ;
QADRI, SB ;
FOLEY, JC ;
PEREPEZKO, JH .
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 1995, 195 (1-2) :13-19
[9]  
FAN WJ, 1994, Z METALLKD, V85, P522
[10]   ALUMINUM NI3AL COMPOSITES PROCESSED BY POWDER-METALLURGY [J].
GONZALEZCARRASCO, JL ;
GARCIACANO, F ;
CARUANA, G ;
LIEBLICH, M .
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 1994, 183 (1-2) :L5-L8