Corrosion of alumina-forming austenitic steel Fe-20Ni-14Cr-3Al-0.6Nb-0.1Ti in supercritical water

被引：56

作者：

Nie, S. H. ^{[1
]}

Chen, Y. ^{[1
]}

Ren, X. ^{[1
]}

Sridharan, K. ^{[1
]}

Allen, T. R. ^{[1
]}

机构：

[1] Univ Wisconsin, Dept Engn Phys, Madison, WI 53706 USA

来源：

JOURNAL OF NUCLEAR MATERIALS | 2010年 / 399卷 / 2-3期

基金：

美国国家科学基金会;

关键词：

STAINLESS-STEELS; CREEP-RESISTANT; SCALE FORMATION; TEMPERATURE; OXIDATION; ADDITIONS; ALLOYS; PHASE;

D O I：

10.1016/j.jnucmat.2010.01.025

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

The oxidation behavior of alumina-forming austenitic (AFA) steel Fe-20Ni-14Cr-3Al-0.6Nb-0.1Ti has been examined after exposure to supercritical water (SCW) at 500 degrees C and 25 MPa pressure and with a dissolved oxygen content of 25 wppb, for exposure periods of 1300 h, 1700 h and 3000 h. A double layer oxide structure developed on all samples, consisting specifically of a Fe-rich outer hematite layer and an inner layer of Al-Cr-Fe-rich oxide containing a small fraction of FCC Ni-rich metal. Additionally, a thin Ni-rich layer in the bulk alloy close to the oxide/metal interface was also observed. Based on weight gain measurements, the oxidation resistance of the AFA steel was superior to other austenitic alloys, 800H, D9, and 316 stainless steel, tested under similar conditions. The formation of the protective Al-Cr-Fe-rich oxide layer may provide good long-term protection against corrosion in SCW environment. (C) 2010 Elsevier B.V. All rights reserved.

引用

页码：231 / 235

页数：5

共 24 条

[21] Alumina-forming austenitic stainless steels strengthened by laves phase and MC carbide precipitates [J].

Yamamoto, Y. ;

Brady, M. P. ;

Lu, Z. P. ;

Liu, C. T. ;

Takeyama, M. ;

Maziasz, P. J. ;

Pint, B. A. .

METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 2007, 38A (11) :2737-2746

[22] Creep-resistant, Al2O3-forming austenitic stainless steels [J].

Yamamoto, Y. ;

Brady, M. P. ;

Lu, Z. P. ;

Maziasz, P. J. ;

Liu, C. T. ;

Pint, B. A. ;

More, K. L. ;

Meyer, H. M. ;

Payzant, E. A. .

SCIENCE, 2007, 316 (5823) :433-436

[23] Effect of Alloying Additions on Phase Equilibria and Creep Resistance of Alumina-Forming Austenitic Stainless Steels [J].

Yamamoto, Y. ;

Santella, M. L. ;

Brady, M. P. ;

Bei, H. ;

Maziasz, P. J. .

METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 2009, 40A (08) :1868-1880

[24]

YUREK GJ, 1987, CORROSION MECH, P398

← 1 2 3 →