Meso/macroporous carbon monoliths from polymeric foams

被引：44
作者：
Alvarez, S
Esquena, J
Solans, C
Fuertes, AB
机构：
[1] CSIC, Inst Nacl Carbon, E-33080 Oviedo, Spain
[2] CSIC, Inst Invest Quim & Ambientals Barcelona, E-08034 Barcelona, Spain
来源：
ADVANCED ENGINEERING MATERIALS | 2004年 / 6卷 / 11期
关键词：
D O I：
10.1002/adem.200400109
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
The synthesis of meso/macroporous carbon monoliths from polymeric foams was investigated. The monoliths were obtained by templating mesostructured silica monoliths by using macroporous polystyrene foams as structure scaffolds. The TEM and SEM were used to analyze the structure of the sample monolith. The cellulose structure of the polystyrene foams was preserved in the carbon monoliths, which exhibited a fully interconnected macroporous network composed of hierarchically organised cells. The carbon skeletal was found to contain a large framework-confined porosity made up of uniform mesopores.
引用
收藏
页码：897 / 899
页数：3
相关论文
共 14 条
[1]   Highly concentrated W/O emulsions prepared by the PIT method as templates for solid foams [J].
Esquena, J ;
Sankar, GR ;
Solans, C .
LANGMUIR, 2003, 19 (07) :2983-2988
[2]   Template synthesis of mesoporous carbons from mesostructured silica by vapor deposition polymerisation [J].
Fuertes, AB ;
Nevskaia, DM .
JOURNAL OF MATERIALS CHEMISTRY, 2003, 13 (07) :1843-1846
[3]   Control of mesoporous structure of carbons synthesised using a mesostructured silica as template [J].
Fuertes, AB ;
Nevskaia, DM .
MICROPOROUS AND MESOPOROUS MATERIALS, 2003, 62 (03) :177-190
[4]   Template synthesis of carbon nanotubules by vapor deposition polymerization [J].
Fuertes, AB .
CARBON, 2002, 40 (09) :1600-1602
[5]   Direct preparation of nanoporous carbon by nanocasting [J].
Han, BH ;
Zhou, WZ ;
Sayari, A .
JOURNAL OF THE AMERICAN CHEMICAL SOCIETY, 2003, 125 (12) :3444-3445
[6]   Synthesis of new, nanoporous carbon with hexagonally ordered mesostructure [J].
Jun, S ;
Joo, SH ;
Ryoo, R ;
Kruk, M ;
Jaroniec, M ;
Liu, Z ;
Ohsuna, T ;
Terasaki, O .
JOURNAL OF THE AMERICAN CHEMICAL SOCIETY, 2000, 122 (43) :10712-10713
[7]   A low cost route to hexagonal mesostructured carbon molecular sieves [J].
Kim, SS ;
Pinnavaia, TJ .
CHEMICAL COMMUNICATIONS, 2001, (23) :2418-2419
[8]   Application of large pore MCM-41 molecular sieves to improve pore size analysis using nitrogen adsorption measurements [J].
Kruk, M ;
Jaroniec, M ;
Sayari, A .
LANGMUIR, 1997, 13 (23) :6267-6273
[9]   Meso/macroporous inorganic oxide monoliths from polymer foams [J].
Maekawa, H ;
Esquena, J ;
Bishop, S ;
Solans, C ;
Chmelka, BF .
ADVANCED MATERIALS, 2003, 15 (7-8) :591-596
[10]   Synthesis of highly ordered carbon molecular sieves via template-mediated structural transformation [J].
Ryoo, R ;
Joo, SH ;
Jun, S .
JOURNAL OF PHYSICAL CHEMISTRY B, 1999, 103 (37) :7743-7746
12