Delamination onset in symmetric cross-ply laminates under static loads: Theory, numerics and experiments

被引：28

作者：

Carraro, Paolo Andrea ^{[1
]}

Novello, Elisa ^{[1
]}

Quaresimin, Marino ^{[1
]}

Zappalorto, Michele ^{[1
]}

机构：

[1] Univ Padua, Dept Management & Engn, Str S Nicola 3, Vicenza, Italy

来源：

COMPOSITE STRUCTURES | 2017年 / 176卷

关键词：

Delamination; Transverse cracks; Cross ply laminates; Generalized Stress Intensity Factors; STRESS INTENSITY FACTOR; CRACK INDUCED DELAMINATION; INTERFACE RELATED DAMAGE; MIXED-MODE DELAMINATION; LAP BONDED JOINTS; FATIGUE DELAMINATION; TRANSVERSE CRACKING; FRACTURE INITIATION; SHARP NOTCHES; PART II;

D O I：

10.1016/j.compstruct.2017.05.030

中图分类号：

O3 [力学];

学科分类号：

08 ; 0801 ;

摘要：

In this paper, the delamination onset from transverse cracks in composite cross-ply laminates under static loadings is thoroughly investigated. Initially, an analytical solution is presented for the local mode I, II and III stress fields arising in the close neighbourhoods of a transverse crack, stresses being written as a function of Generalized Stress Intensity Factors (GSIFs). Then, a fracture criterion for the delamination onset in cross-ply laminates under tension, based on a critical value for the mode 1 GSIF, is proposed and validated taking advantage of the results from an experimental campaign carried out in the present work, as well as reconsidering some data taken from the literature. (C) 2017 Elsevier Ltd. All rights reserved.

引用

页码：420 / 432

页数：13

共 50 条

[41] Effects of Interfacial Damage on the Global and Local Static Response of Cross-Ply Laminates
M. Di Sciuva
U. Icardi
L. Librescu
International Journal of Fracture, 1999, 96 : 17 - 35
[42] A probabilistic static fatigue model for transverse cracking in CFRP cross-ply laminates
Ogi, Keiji
Yashiro, Shigeki
Takahashi, Manabu
Ogihara, Shinji
COMPOSITES SCIENCE AND TECHNOLOGY, 2009, 69 (3-4) : 469 - 476
[43] THE BEHAVIOR OF CRACKED CROSS-PLY COMPOSITE LAMINATES UNDER SHEAR LOADING
TSAI, CL
DANIEL, IM
INTERNATIONAL JOURNAL OF SOLIDS AND STRUCTURES, 1992, 29 (24) : 3251 - 3267
[44] INTERLAYER SHEAR SLIP THEORY FOR CROSS-PLY LAMINATES WITH NONRIGID INTERFACES
LU, X
LIU, D
AIAA JOURNAL, 1992, 30 (04) : 1063 - 1073
[45] Analysis of a radial crack in cross-ply laminates under uniaxial tension
Seong-Kyun Cheong
Oh-Nam Kwon
KSME International Journal, 1997, 11 : 650 - 656
[46] Damage evolution in cross-ply laminates under tension-compression and compression-compression cyclic loads
Carraro, P. A.
Maragoni, L.
Quaresimin, M.
COMPOSITES PART A-APPLIED SCIENCE AND MANUFACTURING, 2022, 156
[47] Analysis of a radial crack in cross-ply laminates under uniaxial tension
Cheong, SK
Kwon, ON
KSME INTERNATIONAL JOURNAL, 1997, 11 (06): : 650 - 656
[48] Interaction of Matrix Cracking and Delamination in Cross-ply Laminates: Simulations with Stochastic Cohesive Zone Elements
Khokhar, Zahid R.
Ashcroft, Ian A.
Silberschmidt, Vadim V.
APPLIED COMPOSITE MATERIALS, 2011, 18 (01) : 3 - 16
[49] Describing the Flexural Behaviour of Cross-ply Laminates Under Cyclic Fatigue
Abderrahim El Mahi
Abderrezak Bezazi
Applied Composite Materials, 2009, 16
[50] Variational solutions to stresses in cracked cross-ply laminates under bending
Kuriakose, S
Talreja, R
INTERNATIONAL JOURNAL OF SOLIDS AND STRUCTURES, 2004, 41 (9-10) : 2331 - 2347

← 1 2 3 4 5 →