Hot corrosion of SiO2-Ta2O5 binary scale on MoSi2-based ceramics

被引:3
作者
Sun, Le [1 ]
Fu, Qian-Gang [1 ]
Sun, Jia [1 ]
机构
[1] Northwestern Polytech Univ, Carbon Carbon Composites Res Ctr, State Key Lab Solidificat Proc, Shaanxi Key Lab Fiber Reinforced Light Composite, Xian 710072, Peoples R China
基金
中国国家自然科学基金;
关键词
Ta2O5; Hot corrosion; Na2SO4; MoSi2; Oxidation; PHASE-RELATIONS; BEHAVIOR; VAPOR; TEMPERATURE; RESISTANCE; OXIDATION; ZIRCONIA; TANTALUM; TA2O5;
D O I
10.1016/j.corsci.2021.109413
中图分类号
T [工业技术];
学科分类号
08 ;
摘要
The SiO2-Ta2O5 binary scales with different Ta2O5 contents were prepared on MoSi2-based ceramics by pre-oxidation. Hot corrosion with Na2SO4 was carried out at 1000 degrees C for 8 h. The pre-oxidized SiO2-Ta2O5 scale on ceramics with 10 % Ta2O5 has an excellent hot corrosion resistance. Ta2O5 reacted preferentially with Na2SO4 forming solid sodium tantalates to retard the dissolution of SiO2. A dense reaction layer can be formed to prevent the further infiltration of Na2SO4. Compared to the pure SiO2 scale without Ta2O5, fewer Na2MoO4 and no obvious corrosion hole can be observed.
引用
收藏
页数:9
相关论文
共 33 条
[1]   Resistance of a Mo-Si-B-Based Coating to Environmental Salt-Based Hot Corrosion [J].
Auchter, Eric ;
Taylor, Matthew ;
Perepezko, John H. .
OXIDATION OF METALS, 2020, 93 (3-4) :387-399
[2]   EFFECTS OF TEMPERATURE AND REAGENT CONCENTRATION ON THE MORPHOLOGY OF CHEMICALLY VAPOR-DEPOSITED BETA-TA2O5 [J].
BAE, YW ;
LEE, WY ;
STINTON, DP .
JOURNAL OF THE AMERICAN CERAMIC SOCIETY, 1995, 78 (05) :1297-1300
[3]   Role of tantalum in the hot corrosion of a Ni-base single crystal superalloy [J].
Chang, J. X. ;
Wang, D. ;
Liu, T. ;
Zhang, G. ;
Lou, L. H. ;
Zhang, J. .
CORROSION SCIENCE, 2015, 98 :585-591
[4]  
Fang Y., 2020, SURF COAT TECH
[5]   MECHANISM OF BENEFICIAL EFFECT OF TANTALUM IN HOT CORROSION OF NICKEL-BASE SUPERALLOYS [J].
FRYBURG, GC ;
STEARNS, CA ;
KOHL, FJ .
JOURNAL OF THE ELECTROCHEMICAL SOCIETY, 1977, 124 (07) :1147-1148
[6]   CHEMICAL-REACTIONS INVOLVED IN THE INITIATION OF HOT CORROSION OF B-1900 AND NASA-TRW VIA [J].
FRYBURG, GC ;
KOHL, FJ ;
STEARNS, CA ;
FIELDER, WL .
JOURNAL OF THE ELECTROCHEMICAL SOCIETY, 1982, 129 (03) :571-585
[7]   Microstructure modification of Y2O3 stabilized ZrO2 thermal barrier coatings by laser glazing and the effects on the hot corrosion resistance [J].
Guo, Lei ;
Xin, Hui ;
Zhang, Zhao ;
Zhang, Xinmu ;
Ye, Fuxing .
JOURNAL OF ADVANCED CERAMICS, 2020, 9 (02) :232-242
[8]   Hot corrosion behavior of TiO2 doped, Yb2O3 stabilized zirconia exposed to V2O5 + Na2SO4 molten salt at 700-1000 °C [J].
Guo, Lei ;
Yan, Zheng ;
Yu, Jianxing ;
Zhang, Chenglong ;
Li, Mingzhu ;
Ye, Fuxing ;
Ji, Vincent .
CERAMICS INTERNATIONAL, 2018, 44 (01) :261-268
[9]   Evolution of Hot Corrosion Behavior of YSZ-Ta2O5 Composites with Different YSZ/Ta2O5 Ratios [J].
Habibi, Hamed ;
Guo, Shengmin .
INTERNATIONAL JOURNAL OF APPLIED CERAMIC TECHNOLOGY, 2015, 12 (03) :542-550
[10]   Phase stability and hot corrosion behavior of ZrO2-Ta2O5 compound in Na2SO4-V2O5 mixtures at elevated temperatures [J].
Habibi, M. H. ;
Yang, Shizhong ;
Guo, S. M. .
CERAMICS INTERNATIONAL, 2014, 40 (03) :4077-4083