Structure and forming process of the Ti/Al diffusion bonding joints

被引：0

作者：

Yao Wei ^{[1
]}

Wu Aiping ^{[1
]}

Zou Guisheng ^{[1
]}

Ren Halie ^{[1
]}

机构：

[1] Tsinghua Univ, Minist Educ, Key Lab Adv Mat Proc Technol, Beijing 100084, Peoples R China

来源：

RARE METAL MATERIALS AND ENGINEERING | 2007年 / 36卷 / 04期

关键词：

diffusion bonding; diffusion reaction; joint structure;

D O I：

暂无

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

Structure and forming process of the Ti/Al diffusion bonding joints were studied by means of scanning electron microscopy (SEM), X-ray diffractometry (XRD) and shear strength measurement. The TA2 and L4 were used as bonding couples. The results showed that the forming process of joints included four stages. The primary and unique phase was TiAl3 from the diffusion reaction for long time. There was a delay time t(D) before TiAl3 appeared, mainly affected by temperature. The joint strength depended on the metallurgical combination percentage and interface structure of diffusion zone, reaching or even exceeding the strength of L4 when the TiAl3 formed like sheet and layer. The shearing fracture of joints occurred on the interface of Al and diffusion zone or in the Al-based metal.

引用

页码：700 / 704

页数：5

共 12 条

[1] Void formation by the reactive diffusion of titanium and aluminum foils [J].

Fukutomi, H ;

Nakamura, M ;

Suzuki, T ;

Takagi, S ;

Kikuchi, S .

MATERIALS TRANSACTIONS JIM, 2000, 41 (09) :1244-1246

[2]

HE KS, 1982, MAT DIFFUSION WELDIN

[3]

HE KS, 1986, DISSIMILAR METAL WEL

[4] THERMODYNAMIC ASSESSMENT AND CALCULATION OF THE TI-AL SYSTEM [J].

KATTNER, UR ;

LIN, JC ;

CHANG, YA .

METALLURGICAL TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 1992, 23 (08) :2081-2090

[5]

LIU ZQ, 1997, MANUAL DISSIMILAR ME

[6]

Luo JG, 2000, WELD J, V79, p239S

[7] Using cold roll bonding and annealing to process Ti/Al multi-layered composites from elemental foils [J].

Luo, JG ;

Acoff, VL .

MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2004, 379 (1-2) :164-172

[8] Processing and mechanical behavior of laminated titanium-titanium tri-aluminide (Ti-Al3 Ti) composites [J].

Peng, LM ;

Li, H ;

Wang, JH .

MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2005, 406 (1-2) :309-318

[9] Microstructure characteristics in the interface zone of Ti/Al diffusion bonding [J].

Ren, JW ;

Li, YJ ;

Feng, T .

MATERIALS LETTERS, 2002, 56 (05) :647-652

[10]

SONG TH, 2001, WELDING MANUAL

← 1 2 →