Evaluation of lifetime of FGMs disilicide coatings for γ-TiAl intermetallic compound

被引：0
|
作者：
Ohshima, Masayuki [1 ]
Abu Suilik, Saleh B. [1 ]
Tetsui, Toshimitsu [2 ]
Hasezaki, Kazuhiro [1 ]
机构：
[1] Shimane Univ, Dept Mat Sci, Nishikawatsu Cho 1060, Matsue, Shimane 6908504, Japan
[2] Tohoku Univ, Inst Mat Res, Sendai, Miyagi 9808577, Japan
来源：
MULTISCALE, MULTIFUNCTIONAL AND FUNCTIONALLY GRADED MATERIALS | 2010年 / 631-632卷
关键词：
Titanium aluminide; intermetallic compound; lifetime; siliconization; molten salts; oxidation resistance coatings; general oxidation; volume diffusion; OXIDATION BEHAVIOR;
D O I：
10.4028/www.scientific.net/MSF.631-632.495
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
The NbSi2/Nb/gamma-TiAl and NbSi2/Nb functionally graded materials (FGMs) were prepared and their tolerances tested by exposing them to temperatures from 1050 degrees C to 1250 degrees C under vacuum and in air. Oxygen resistivity was estimated from metallographic investigations. The FGM lifetime was estimated by using a diffusion equation that considers the disappearance of the NbSi2 and Nb interlayer. These occurred during NbSi2 oxidation and Si diffusion from NbSi2 to Nb and interdiffusion between Nb and gamma-TiAl. The results were validated by diffusion equations.
引用
收藏
页码：495 / +
页数：2
相关论文
共 50 条
  • [1] Empirical analysis of lifetimes for disilicide coatings on a γ-TiAl intermetallic compound
    Ohshima, Masayuki
    Tetsui, Toshimitsu
    Hasezaki, Kazuhiro
    Funtai Oyobi Fummatsu Yakin/Journal of the Japan Society of Powder and Powder Metallurgy, 2009, 56 (07): : 444 - 448
  • [2] Preparation and high temperature oxidation behavior of refractory disilicide coatings for γ-TiAl intermetallic compounds
    Abu Suilik, Saleh B.
    Takeshita, Ken
    Kitagawa, Hiroyuki
    Tetsui, Toshimitsu
    Hasezaki, Kazuhiro
    INTERMETALLICS, 2007, 15 (08) : 1084 - 1090
  • [3] Characteristics of coatings fabricated by microarc oxidation on TiAl intermetallic compound
    Li, Xi-Jin
    Cheng, Guo-An
    Xue, Wen-Bin
    Zheng, Rui-Ting
    Wu, Xiao-Ling
    Cheng, Yun-Jun
    Cailiao Rechuli Xuebao/Transactions of Materials and Heat Treatment, 2006, 27 (05): : 95 - 99
  • [4] PROPERTIES OF THE INTERMETALLIC COMPOUND TiAl
    邢胜娣
    ChineseScienceBulletin, 1992, (03) : 235 - 239
  • [5] PROPERTIES OF THE INTERMETALLIC COMPOUND TIAL
    XING, SD
    CHINESE SCIENCE BULLETIN, 1992, 37 (03): : 235 - 239
  • [6] Impact strength of γ-TiAl intermetallic compound
    Ogawa, Kinya
    Bandou, Hiroshi
    Sugiyama, Fumiko
    Nippon Kikai Gakkai Ronbunshu, A Hen/Transactions of the Japan Society of Mechanical Engineers, Part A, 1995, 61 (590): : 2247 - 2252
  • [7] DEFORMATION MECHANISMS IN THE INTERMETALLIC COMPOUND TIAL
    COURT, SA
    VASUDEVAN, VK
    FRASER, HL
    PHILOSOPHICAL MAGAZINE A-PHYSICS OF CONDENSED MATTER STRUCTURE DEFECTS AND MECHANICAL PROPERTIES, 1990, 61 (01): : 141 - 158
  • [8] Laser piercing of TiAl intermetallic compound
    Shigematsu, Ichinori
    Nakamura, Mamoru
    Kanayama, Kouzou
    Kozuka, Teruyuki
    Keikinzoku/Journal of Japan Institute of Light Metals, 1993, 43 (03): : 159 - 164
  • [9] DIFFUSION BONDING OF INTERMETALLIC COMPOUND TIAL
    NAKAO, Y
    SHINOZAKI, K
    HAMADA, M
    ISIJ INTERNATIONAL, 1991, 31 (10) : 1260 - 1266
  • [10] Solute diffusion in the intermetallic compound γ-TiAl
    Przeorski, T
    Friesel, M
    Hisker, F
    Divinski, SV
    Herzig, C
    DIFFUSIONS IN MATERIALS: DIMAT2000, PTS 1 & 2, 2001, 194-1 : 493 - 498
12345