Failure analysis of a cast steel railway wheel

被引：23
作者：
Fuoco, R [1 ]
Ferreira, MM [1 ]
Azevedo, CRF [1 ]
机构：
[1] Inst Pesquisas Tecnol Estado Sao Paulo SA, Div Met, BR-01064970 Sao Paulo, Brazil
来源：
ENGINEERING FAILURE ANALYSIS | 2004年 / 11卷 / 06期
基金：
巴西圣保罗研究基金会;
关键词：
failure analysis; fractography; cast steel; fatigue; railway engineering;
D O I：
10.1016/j.engfailanal.2004.03.004
中图分类号：
TH [机械、仪表工业];
学科分类号：
0802 ;
摘要：
The failure analysis of a broken railway pearlitic cast steel railway wheel, which was involved in a train derailment, has been investigated. The fractographic results near the fracture origin of the wheel have been compared to the regions of stable (fatigue) and unstable crack propagation of cast steel fracture toughness samples. The macro and microfractographic features of the broken wheel did not show any evidence of the occurrence of a fatigue mechanism, indicating that its fracture was caused by transgranular cleavage fracture, as a consequence of the train derailment. (C) 2004 Elsevier Ltd. All rights reserved.
引用
收藏
页码：817 / 828
页数：12
相关论文
共 50 条
  • [1] Failure mechanism analysis on railway wheel shaft of power locomotive
    Zhu, Chongfei
    He, Jifan
    Peng, Jinfang
    Ren, Yanping
    Liu, Xiuzhou
    Zhu, Minhao
    ENGINEERING FAILURE ANALYSIS, 2019, 104 : 25 - 38
  • [2] Fatigue crack failure analysis of wrought steel railway wheel with web plate hole
    Zheng, HX
    Xie, JL
    Wang, WJ
    Proceedings of the International Conference on Mechanical Engineering and Mechanics 2005, Vols 1 and 2, 2005, : 1471 - 1474
  • [3] Random Critical Fracture Toughness Values of China Railway Grade B Cast Steel Wheel
    Chen, L.
    Zhao, Y. X.
    Song, G. X.
    MATERIALS ENGINEERING FOR ADVANCED TECHNOLOGIES, PTS 1 AND 2, 2011, 480-481 : 381 - +
  • [4] Random Fatigue Crack Growth Rates of China Railway Grade B Cast Steel Wheel
    Zhao, Y. X.
    Yang, B.
    Song, G. X.
    MATERIALS ENGINEERING FOR ADVANCED TECHNOLOGIES, PTS 1 AND 2, 2011, 480-481 : 387 - +
  • [5] Study on fatigue failure mechanism at various temperatures of a high-speed railway wheel steel
    Fang, Xiu-Yang
    Zhao, Yong-Xiang
    Liu, Huan-Wei
    MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2017, 696 : 299 - 314
  • [6] Production of High-Quality Wheel Steel. Part 1. Production Aspects of Continuously-Cast Billet Quality for Railway Wheel Manufacture
    Pumpyanskiy, D. A.
    Tyutyunik, S. V.
    Kolokolov, E. A.
    Mescheryachenko, A. A.
    Murzin, I. S.
    Emel'yanov, V. V.
    Belonozhko, S. S.
    Arsenkin, A. M.
    METALLURGIST, 2021, 65 (1-2) : 13 - 20
  • [7] Numerical thermo-mechanical analysis of a railway train wheel
    Bulut, Mehmet
    Karagoz, Nail
    Acar, Halil
    Duman, Netice
    MATERIALS TESTING, 2023, 65 (05) : 733 - 742
  • [8] Mixed mode fatigue crack propagation in a railway wheel steel
    Peixoto, Daniel F. C.
    de Castro, Paulo M. S. T.
    XV PORTUGUESE CONFERENCE ON FRACTURE, PCF 2016, 2016, 1 : 150 - 157
  • [9] Fatigue Investigation on Railway Wheel Steel with White Etching Layer
    Zhang, Y. M.
    Xiao, Z. M.
    Fan, M.
    INTERNATIONAL JOURNAL OF STEEL STRUCTURES, 2020, 20 (01) : 80 - 88
  • [10] Fatigue Investigation on Railway Wheel Steel with White Etching Layer
    Y. M. Zhang
    Z. M. Xiao
    M. Fan
    International Journal of Steel Structures, 2020, 20 : 80 - 88
12345