Investigation of corrosion rate of X55CrMo14 stainless steel at 65% nitrate acid at 348 K

被引:12
作者
Lipinski, Tomasz [1 ]
机构
[1] Univ Warmia & Mazury, Oczapowskiego 11 St, PL-10957 Olsztyn, Poland
关键词
steel; stainless steel; corrosion; corrosion rate; profile roughness; RESISTANCE; QUALITY; MICROSTRUCTURE;
D O I
10.30657/pea.2021.27.13
中图分类号
T [工业技术];
学科分类号
08 ;
摘要
A number of factors determine the mechanical, but also physical and chemical properties. One of the most important are the steel microstructure and its working conditions. A few corrosion processes in crevices and awkward corners can be avoided at the design stage (low roughness parameters, round-section and other). But still the construction material is exposed to corrosion. These steels often come into contact with an aggressive environment based on nitric acid. Stainless steel is more and more often used in many sectors of industry. The purpose of this article is to investigate corrosion resistance in different time (48, 96, 144, 192, 240, 288, 336, 384 and 432 hours) using weight loss and profile roughness parameters of martensitic steel in grade X55CrMo14 in nitric acid 65% pure-basic at temperature 348 K. Corrosion tests show that the tested steel in nitric acid as a corrosive environments is characterized through continuous corrosion process whose measure may be surface roughness.
引用
收藏
页码:108 / 111
页数:4
相关论文
共 32 条
  • [1] Cheng X.L., 1998, Corrosion of Iron in Acid Solutions with Hydrogen Sulfide Corrosion Sciences, V41, P321
  • [2] On the onset of necking instability in tempered martensitic 9% Cr steels
    Christopher, J.
    Choudhary, B. K.
    [J]. MECHANICS RESEARCH COMMUNICATIONS, 2018, 94 : 114 - 119
  • [3] Degradation mechanisms in martensitic stainless steels: Wear, corrosion and tribocorrosion appraisal
    Dalmau, A.
    Richard, C.
    Igual-Munoz, A.
    [J]. TRIBOLOGY INTERNATIONAL, 2018, 121 : 167 - 179
  • [4] Surface remelting of 316 L+434 L sintered steel: microstructure and corrosion resistance
    Dudek, Agata
    Wronska, Agata
    Adamczyk, Lidia
    [J]. JOURNAL OF SOLID STATE ELECTROCHEMISTRY, 2014, 18 (11) : 2973 - 2981
  • [5] Evaluation of temperature fields in corrosion-resistant steels under the action of laser radiation
    Duryahina, Z. A.
    Makhorkin, I. M.
    Laz'ko, H. V.
    Bychyns'kyi, V. I.
    [J]. MATERIALS SCIENCE, 2007, 43 (06) : 800 - 806
  • [6] Hot workability of 420 J1 martensitic stainless steel
    El-Meligy, Maha
    El-Bitar, Taher
    [J]. 18TH INTERNATIONAL CONFERENCE ON METAL FORMING 2020, 2020, 50 : 771 - 776
  • [7] Modeling the cyclic softening and lifetime of ferritic-martensitic steels under creep-fatigue loading
    Fuehrer, Ulrich
    Aktaa, Jarir
    [J]. INTERNATIONAL JOURNAL OF MECHANICAL SCIENCES, 2018, 136 : 460 - 474
  • [8] Krynke M., 2012, Materials Engineering - Materialoveinzinierstvo vo, V19, P157, DOI [10.1007/s12206-011-1203-4, DOI 10.1007/S12206-011-1203-4]
  • [9] Corrosion Rate of the X2CrNiMoN22-5-3 Duplex Stainless Steel Annealed at 500 °C
    Lipinski, T.
    [J]. ACTA PHYSICA POLONICA A, 2016, 130 (04) : 993 - 995
  • [10] Lipinski Tomasz, 2015, Solid State Phenomena, V223, P46, DOI 10.4028/www.scientific.net/SSP.223.46