Tribological behavior of PTFE film with nanodiamond

被引：72

作者：

Lee, JY ^{[1
]}

Lim, DS ^{[1
]}

机构：

[1] Korea Univ, Dept Mat Sci & Engn, Seoul 136701, South Korea

来源：

SURFACE & COATINGS TECHNOLOGY | 2004年 / 188卷

关键词：

PTFE; nanodiamond; wear; SEM; TEM;

D O I：

10.1016/j.surfcoat.2004.07.102

中图分类号：

TB3 [工程材料学];

学科分类号：

0805 ; 080502 ;

摘要：

The effect of nanodiamond addition on the tribological behavior of polytetrafluoroethylene (PTFE) film was investigated. Nanodiamond particles produced by detonation method were added up to 4 wt.% to PTFE film to improve the wear resistance and thermal stability. Tribological tests of nanodiamond-reinforced PTFE coatings were performed by using a ball-on-plate reciprocating wear tester at room temperature and 150 degreesC. The wear resistance of PTFE composite coating was increased with increasing content of nanodiamond up to 2 wt.% but decreased slightly with further addition of nanodiamond at tested temperature ranges. The coefficient of friction and width of wear track changed from 0.21 to 0.16 and 0.85 to 0.44 mm, respectively, when 2 wt.% of nanodiamond was added to PTFE. Possible mechanisms for enhancement of tribological properties by nanodiamond additions were discussed based on SEM and TEM observation. This study showed that nanodiamond was well dispersed and enhanced the tribological properties of PTFE by hardening PTFE composite with nanodiamond and by the self-lubricating effect between PTFE composite film and sliding ball. (C) 2004 Elsevier B.V. All rights reserved.

引用

页码：534 / 538

页数：5

共 15 条

[1] Tribological investigation of PTFE composite filled with lead and rare earths-modified glass fiber [J].

Cheng, XH ;

Xue, YJ ;

Xie, CY .

MATERIALS LETTERS, 2003, 57 (16-17) :2553-2557

[2] Filler-polymer interactions in filled polybutadiene compounds [J].

Choi, SS ;

Kim, IS .

EUROPEAN POLYMER JOURNAL, 2002, 38 (06) :1265-1269

[3] DIAMONDS IN DETONATION SOOT [J].

GREINER, NR ;

PHILLIPS, DS ;

JOHNSON, JD ;

VOLK, F .

NATURE, 1988, 333 (6172) :440-442

[4] Mechanical properties of glass-ceramic A-W-polyethylene composites: effect of filler content and particle size [J].

Juhasz, JA ;

Best, SM ;

Brooks, R ;

Kawashita, M ;

Miyata, N ;

Kokubo, T ;

Nakamura, T ;

Bonfield, W .

BIOMATERIALS, 2004, 25 (06) :949-955

[5] The friction and wear characteristics of nanometer ZnO filled polytetrafluoroethylene [J].

Li, F ;

Hu, KA ;

Li, JL ;

Zhao, BY .

WEAR, 2001, 249 (10-11) :877-882

[6]

MANDICH NV, 2001, MET FINISH, P117

[7] Carbon nanocomposite materials as medicinal depot [J].

Ostrovidova, GU ;

Makeev, AV ;

Biryukov, AV ;

Gordeev, SK .

MATERIALS SCIENCE & ENGINEERING C-BIOMIMETIC AND SUPRAMOLECULAR SYSTEMS, 2003, 23 (03) :377-381

[8] A study on the friction and wear behavior of PTFE filled with alumina nanoparticles [J].

Sawyer, WG ;

Freudenberg, KD ;

Bhimaraj, P ;

Schadler, LS .

WEAR, 2003, 254 (5-6) :573-580

[9] Surface profiles of composites with PTFE matrix [J].

Tomescu, L ;

Rîpa, M ;

Vasilescu, E ;

Georgescu, C .

JOURNAL OF MATERIALS PROCESSING TECHNOLOGY, 2003, 143 :384-389

[10] Sliding friction and wear behaviour of polytetrafluoroethylene and its composites under dry conditions [J].

Unal, H ;

Mimaroglu, A ;

Kadioglu, U ;

Ekiz, H .

MATERIALS & DESIGN, 2004, 25 (03) :239-245

← 1 2 →