Synthesis and compressibility of Ti3(Al,Sn0.2)C2 and Ti3Al(C0.5,N0.5)2

被引:75
作者
Manoun, Bouchaib
Saxena, S. K.
Hug, Gilles
Ganguly, A.
Hoffman, E. N.
Barsoum, M. W.
机构
[1] Off Natl Etud & Rech Aerosp, CNRS, Lab Etud Microstruct, F-92322 Chatillon, France
[2] Florida Int Univ, CeSMEC, Miami, FL 33199 USA
[3] Univ Penn, Dept Mat Sci & Engn, Philadelphia, PA 19104 USA
基金
美国国家科学基金会;
关键词
D O I
10.1063/1.2733644
中图分类号
O59 [应用物理学];
学科分类号
摘要
In this paper we report on the synthesis of a composition, Ti3Al(C-0.5,N-0.5)(2), belonging to the M(n+1)AX(n) family of ternary layered carbides and nitrides. X-ray and selected area diffraction confirm that this compound is isostructural with Ti3SiC2; its a and c-lattice parameters are 3.0404(5) and 18.414(6) A, respectively. Chemical analysis performed by electron dispersive and electron energy loss spectroscopy confirmed the Ti3AlCN chemistry. Using a synchrotron radiation source and a diamond anvil cell, we also measured the pressure dependencies of the lattice parameters. Up to a pressure of approximate to 50 GPa, no phase transformations were observed. The bulk modulus is 219 +/- 4 GPa, with a pressure derivative, K-o('), of 3.7 +/- 0.3. We also fabricated the ternary Ti3AlC2, with some Sn [nominal composition Ti-3(AlSn0.2)C-2]. Its a and c-lattice parameters are 3.0804(7) and 18.5426(7) A, respectively. Its bulk modulus is 226 +/- 3 GPa, with a pressure derivative, K-o('), of approximate to 4. In both cases, the compressibility was greater along the c than along the a axes. We also show that in the case of Tin+1AlCn MAX-phases, replacing C by N results in a decrease in both lattice parameters and bulk moduli. The apparent contradiction inherent in this observation can be reconciled by assuming that the addition of N results in the formation of vacancies on the Al and/or X-sites. (c) 2007 American Institute of Physics.
引用
收藏
页数:7
相关论文
共 54 条
[1]  
Ai MX, 2006, J AM CERAM SOC, V89, P1114, DOI [10.1111/j.1551-29162005.00818.x, 10.1111/j.1551-2916.2005.00818.x]
[2]   Processing and characterization of Ti2AlC, Ti2AlN, and Ti2AlC0.5N0.5 [J].
Barsoum, MW ;
Ali, M ;
El-Raghy, T .
METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 2000, 31 (07) :1857-1865
[3]  
Barsoum MW, 1997, J MATER SYNTH PROCES, V5, P197
[4]   Long time oxidation study of Ti3SiC2,Ti3SiC2/SiC, and Ti3SiC2/TiC composites in air [J].
Barsoum, MW ;
Ho-Duc, LH ;
Radovic, M ;
El-Raghy, T .
JOURNAL OF THE ELECTROCHEMICAL SOCIETY, 2003, 150 (04) :B166-B175
[5]   The MN+1AXN phases:: A new class of solids;: Thermodynamically stable nanolaminates [J].
Barsoum, MW .
PROGRESS IN SOLID STATE CHEMISTRY, 2000, 28 (1-4) :201-281
[6]   Fully reversible, dislocation-based compressive deformation of Ti3SiC2 to 1GPa [J].
Barsoum, MW ;
Zhen, T ;
Kalidindi, SR ;
Radovic, M ;
Murugaiah, A .
NATURE MATERIALS, 2003, 2 (02) :107-111
[7]   Layered machinable ceramics for high temperature applications [J].
Barsoum, MW ;
Brodkin, D ;
ElRaghy, T .
SCRIPTA MATERIALIA, 1997, 36 (05) :535-541
[8]   High-resolution transmission electron microscopy of Ti4AlN3, or Ti3Al2N2 revisited [J].
Barsoum, MW ;
Farber, L ;
Levin, I ;
Procopio, A ;
El-Raghy, T ;
Berner, A .
JOURNAL OF THE AMERICAN CERAMIC SOCIETY, 1999, 82 (09) :2545-2547
[9]   Oxidation of Ti3SiC2 in air [J].
Barsoum, MW ;
ElRaghy, T ;
Ogbuji, LUJT .
JOURNAL OF THE ELECTROCHEMICAL SOCIETY, 1997, 144 (07) :2508-2516
[10]   Thermal properties of Ti3SiC2 [J].
Barsoum, MW ;
El-Raghy, T ;
Rawn, CJ ;
Porter, WD ;
Wang, H ;
Payzant, EA ;
Hubbard, CR .
JOURNAL OF PHYSICS AND CHEMISTRY OF SOLIDS, 1999, 60 (04) :429-439