Influence of Cr addition on microstructure of vacuum brazed NiCr-Cr3C2 composite coatings

被引：9
作者：
Wang, De [1 ]
Xie, Yujiang [1 ,2 ]
Yang, Yanhong [2 ]
Wang, Mingsheng [2 ]
Wang, Wenqin [3 ]
Cheng, Xiangping [1 ]
Lu, Deping [1 ]
机构：
[1] Jiangxi Acad Sci, Appl Phys Res Inst, Nanchang 330026, Peoples R China
[2] Chinese Acad Sci, Inst Met Res, Shenyang 110016, Peoples R China
[3] Nanchang Univ, Sch Mech & Elect Engn, Nanchang 330031, Peoples R China
来源：
MATERIALS CHARACTERIZATION | 2016年 / 115卷
基金：
中国国家自然科学基金;
关键词：
Vacuum brazing; Composite coatings; Superalloy; TEMPERATURE; NICKEL; WEAR; MECHANISM; BEHAVIOR;
D O I：
10.1016/j.matchar.2016.03.016
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
Metallurgically bonded NiCr-Cr3C2 composite coatings modified by the additions of Cr were produced on a Ni-based superalloy substrate by high temperature vacuum brazing process. Effects of Cr addition on the microstructure, phases presented and the interfacial diffusion of the coatings have been investigated. Results show that the Cr additive consumed Si element to form Cr3Si and reduced the amount of brittle phase Ni3Si at the interface. The higher was the Cr addition in the coating, the thinner was the thickness of the secondary reaction zone, and the lower was the amount of the Ni3Si at the interface. (C) 2016 Elsevier Inc All rights reserved.
引用
收藏
页码：46 / 54
页数：9
相关论文
共 27 条
  • [11] Lu Jin-bin, 2010, Chinese Journal of Nonferrous Metals, V20, P137
  • [12] Wear behavior of brazed WC/NiCrBSi(Co) composite coatings
    Lu, SP
    Kwon, OY
    Guo, Y
    [J]. WEAR, 2003, 254 (5-6) : 421 - 428
  • [13] Microstructure and bonding strength of WC reinforced Ni-base alloy brazed composite coating
    Lu, SP
    Kwon, OY
    [J]. SURFACE & COATINGS TECHNOLOGY, 2002, 153 (01) : 40 - 48
  • [14] [马壮 Ma Zhuang], 2012, [热加工工艺, Hot Working Technology], V41, P147
  • [15] High temperature erosion-oxidation of Cr3C2-NiCr thermal spray coatings under simulated turbine conditions
    Matthews, S.
    James, B.
    Hyland, M.
    [J]. CORROSION SCIENCE, 2013, 70 : 203 - 211
  • [16] The role of microstructure in the mechanism of high velocity erosion of Cr3C2-NiCr thermal spray coatings: Part 1-As-sprayed coatings
    Matthews, S.
    James, B.
    Hyland, M.
    [J]. SURFACE & COATINGS TECHNOLOGY, 2009, 203 (08) : 1086 - 1093
  • [17] Fretting fatigue of single crystal nickel at 600 °C
    Murthy, H.
    Gao, G.
    Farris, Thomas N.
    [J]. TRIBOLOGY INTERNATIONAL, 2006, 39 (10) : 1227 - 1240
  • [18] Predel B., 1994, CU SC COPPER SCANDIU, V5D, DOI [10.1007/10086090_1115, DOI 10.1007/10086090_1115]
  • [19] [王炜 WANG Wei], 2009, [北京科技大学学报, Journal of University Science and Technology Beijing], V31, P371
  • [20] Induction brazing of inconel 718 to inconel X-750 using Ni-Cr-Si-B amorphous foil
    Wu, XW
    Chandel, RS
    Li, H
    Seow, HP
    Wu, SC
    [J]. JOURNAL OF MATERIALS PROCESSING TECHNOLOGY, 2000, 104 (1-2) : 34 - 43
123