Influence of Cr addition on microstructure of vacuum brazed NiCr-Cr3C2 composite coatings

被引：9
作者：
Wang, De [1 ]
Xie, Yujiang [1 ,2 ]
Yang, Yanhong [2 ]
Wang, Mingsheng [2 ]
Wang, Wenqin [3 ]
Cheng, Xiangping [1 ]
Lu, Deping [1 ]
机构：
[1] Jiangxi Acad Sci, Appl Phys Res Inst, Nanchang 330026, Peoples R China
[2] Chinese Acad Sci, Inst Met Res, Shenyang 110016, Peoples R China
[3] Nanchang Univ, Sch Mech & Elect Engn, Nanchang 330031, Peoples R China
来源：
MATERIALS CHARACTERIZATION | 2016年 / 115卷
基金：
中国国家自然科学基金;
关键词：
Vacuum brazing; Composite coatings; Superalloy; TEMPERATURE; NICKEL; WEAR; MECHANISM; BEHAVIOR;
D O I：
10.1016/j.matchar.2016.03.016
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
Metallurgically bonded NiCr-Cr3C2 composite coatings modified by the additions of Cr were produced on a Ni-based superalloy substrate by high temperature vacuum brazing process. Effects of Cr addition on the microstructure, phases presented and the interfacial diffusion of the coatings have been investigated. Results show that the Cr additive consumed Si element to form Cr3Si and reduced the amount of brittle phase Ni3Si at the interface. The higher was the Cr addition in the coating, the thinner was the thickness of the secondary reaction zone, and the lower was the amount of the Ni3Si at the interface. (C) 2016 Elsevier Inc All rights reserved.
引用
收藏
页码：46 / 54
页数：9
相关论文
共 27 条
  • [1] Academic Committee of the Superalloys The Chinese Society for Metals, 2012, CHIN SUP HDB
  • [2] Wear as a product failure mechanism - Overview and case studies
    Gagg, Colin R.
    Lewis, Peter R.
    [J]. ENGINEERING FAILURE ANALYSIS, 2007, 14 (08) : 1618 - 1640
  • [3] Guo J., 2008, MAT SCI ENG SUPERALL
  • [4] The Cr-Ni-Si (chromium-nickel-silicon) system
    Gupta, K. P.
    [J]. JOURNAL OF PHASE EQUILIBRIA AND DIFFUSION, 2006, 27 (05) : 523 - 528
  • [5] Interfacial indentation test and adhesive fracture characteristics of plasma sprayed cermet Cr3C2/Ni-Cr coatings
    Hivart, Philippe
    Crampon, Jacques
    [J]. MECHANICS OF MATERIALS, 2007, 39 (11) : 998 - 1005
  • [6] High temperature oxidation studies of detonation-gun-sprayed Cr3C2-NiCr coating on Fe- and Ni-based superalloys in air under cyclic condition at 900°C
    Kamal, Subhash
    Jayaganthan, R.
    Prakash, S.
    [J]. JOURNAL OF ALLOYS AND COMPOUNDS, 2009, 472 (1-2) : 378 - 389
  • [7] Characterization of fretting wear of cobalt-based superalloys at high temperature for aero-engine combustor components
    Korashy, Ahmed
    Attia, Helmi
    Thomson, Vince
    Oskooei, Saeid
    [J]. WEAR, 2015, 330 : 327 - 337
  • [8] Fretting wear characterization by point contact of nickel superalloy interfaces
    Lavella, M.
    Botto, D.
    [J]. WEAR, 2011, 271 (9-10) : 1543 - 1551
  • [9] Comparison of laser-clad and furnace-melted Ni-based alloy microstructures
    Li, Q
    Zhang, DW
    Lei, TQ
    Chen, CZ
    Chen, WZ
    [J]. SURFACE & COATINGS TECHNOLOGY, 2001, 137 (2-3) : 122 - 135
  • [10] Li SP, 2007, ACTA METALL SIN, V43, P439
123