Wetting of Si-14Ti alloy on SiCf/SiC and C/C composites and their brazed joint at high temperatures

被引：23

作者：

He, Zongjing ^{[1
]}

Li, Chun ^{[1
]}

Si, Xiaoqing ^{[1
]}

Qi, Junlei ^{[1
]}

Cao, Jian ^{[1
]}

机构：

[1] Harbin Inst Technol, State Key Lab Adv Welding & Joining, Harbin 150001, Peoples R China

来源：

CERAMICS INTERNATIONAL | 2021年 / 47卷 / 10期

基金：

中国国家自然科学基金;

关键词：

Ceramic-matrix composites; Wetting; Joining; High-temperature mechanical property; MECHANICAL-PROPERTIES; INTERFACIAL MICROSTRUCTURE; POROUS SI3N4; DENSE SI3N4; SI; BEHAVIOR; FILLER; INFILTRATION; WETTABILITY; CARBIDE;

D O I：

10.1016/j.ceramint.2021.01.250

中图分类号：

TQ174 [陶瓷工业]; TB3 [工程材料学];

学科分类号：

0805 ; 080502 ;

摘要：

The wetting and joining of SiCf/SiC composites and C/C composites with a high-temperature Si-14Ti (at. %) braze filler were studied for the first time. Wetting dynamics and the contact angle were investigated by heating the Si-Ti sessile droplets on the SiCf/SiC and the C/C substrates. The interfacial micromorphology, shear strength, and fracture characteristics of the joints were all analysed. The Si-Ti alloy had contact angles of similar to 23. on the C/C and similar to 7. on the SiCf/SiC at 1460 degrees C, demonstrating excellent wettability on both substrates. SiC reaction layers were formed at both interfaces of the joint. The reactive infiltration into both substrates occurred during the brazing process, especially in the SiCf/SiC composites. The infiltration structures and the robust bonding were conducive to strengthening the brazed joint. The joint exhibited optimal shear strength values of 31 MPa at room temperature and 40 MPa at a high temperature of 1000 degrees C.

引用

页码：13845 / 13852

页数：8

共 40 条

[21] Low activation brazing materials and techniques for SiCf/SiC composites [J].

Riccardi, B ;

Nannetti, CA ;

Petrisor, T ;

Sacchetti, M .

JOURNAL OF NUCLEAR MATERIALS, 2002, 307 :1237-1241

[22]

Riccardi B., 2004, INT J MATER PROD TEC, V20

[23] Fabrication of SiCf/SiC and integrated assemblies for nuclear reactor applications [J].

Sharma, Amit Siddharth ;

Fitriani, Pipit ;

Yoon, Dang-Hyok .

CERAMICS INTERNATIONAL, 2017, 43 (18) :17211-17215

[24] Brazing of Gr/2024Al composite and TC4 using AgCuTi filler with the assist of Ti-Al-C-Cu interlayer [J].

Shi, Junmiao ;

Wang, Qian ;

Tian, Xiaoyu ;

Xiong, Jiangtao ;

Li, Jinglong ;

Zhang, Lixia ;

Feng, Jicai .

JOURNAL OF MANUFACTURING PROCESSES, 2019, 47 :211-218

[25] Interfacial microstructure and mechanical property of ZrC-SiC ceramic and TiAl joint brazed with Ag-Zf active filler metal [J].

Shi, Junmiao ;

Wang, Qian ;

Li, Jinglong ;

Xiong, Jiangtao ;

Zhang, Lixia ;

Feng, Jicai .

MATERIALS CHARACTERIZATION, 2019, 156

[26] Characterization of brazed joints of C-C composite to Cu-clad-Molybdenum [J].

Singh, M. ;

Asthana, R. .

COMPOSITES SCIENCE AND TECHNOLOGY, 2008, 68 (14) :3010-3019

[27] Microstructure and mechanical properties of joints in sintered SiC fiber-bonded ceramics brazed with Ag-Cu-Ti alloy [J].

Singh, Mrityunjay ;

Matsunaga, Tadashi ;

Lin, Hua-Tay ;

Asthana, Rajiv ;

Ishikawa, Toshihiro .

MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2012, 557 :69-76

[28] Microstructure and mechanical properties of C/C composite/Ti6Al4V joints with a Cu/TiCuZrNi composite brazing alloy [J].

Song, Xinrui ;

Li, Hejun ;

Casalegno, Valentina ;

Salvo, Milena ;

Ferraris, Monica ;

Zeng, Xierong .

CERAMICS INTERNATIONAL, 2016, 42 (05) :6347-6354

[29] Wetting and joining of porous Si3N4 and dense Si3N4 ceramics with in-situ formed β-spodumene/spinel glass-ceramic interlayer [J].

Sun, Liangbo ;

Liu, Chunfeng ;

Guo, Songsong ;

Fang, Jian ;

Wang, Dongbao ;

Zhang, Jie .

APPLIED SURFACE SCIENCE, 2020, 517 (517)

[30] Joining pre-oxidized dense Si3N4 to porous Si3N4 with β-spodumene based glass-ceramic interlayer [J].

Sun, Liangbo ;

Liu, Chunfeng ;

Zhang, Jie ;

Fang, Jian .

APPLIED SURFACE SCIENCE, 2019, 481 :515-523

← 1 2 3 4 →