The incongruous observation of magnetic phase separation in La0.85Sr0.15CoO3 spin glass system

Phase separation (PS) in hole-doped cobaltites (La1-xSrxCoxO3) is drawing renewed interest recently. In particular, the magnetic behavior of La0.85Sr0.15CoO3 has been subjected to a controversial debate for the past several years; while some groups show evidence for magnetic PS, others show spin glass (SG) behavior. Here, an attempt is made to resolve the controversy related to "PS versus SG" behavior in this compound. We present the results of a comprehensive investigation of the dc magnetization, ac susceptibility, and the magnetotransport properties of La0.85Sr0.15CoO3 samples. We contemplate that the magnetic PS in La0.85Sr0.15CoO3 is neither intrinsic nor inherent, but it is a consequence of the preparation conditions. It is realized that a low temperature annealed (LTA) sample shows PS whereas the high temperature annealed (HTA) sample shows SG behavior. The Brillouin-like behavior of field cooled dc magnetization and apparently no frequency dependent peak shift in ac susceptibility for the LTA sample characterize it to be of ferromagneticlike whereas a kink in field cooled dc magnetization and a considerable amount (similar to 3 K) of frequency dependent peak shift in the ac susceptibility for the HTA sample characterize it to be of SG state. The magnetotransport properties show that the HTA sample is more semiconducting as compared to the LTA sample. This is interpreted in terms of the presence of isolated as well as coalescing metallic ferromagnetic clusters in the case of LTA sample. The magnetoresistance (MR) at 10 K for the HTA sample exhibits a huge value (similar to 65%) as compared to the LTA sample, and it monotonically decreases with the rise in temperature. Such a high value of MR in the case of HTA sample is strongly believed to be due to the spin dependent part of random potential distribution. Further, the slow decay of remnant magnetization with progress of time and the existence of hysteresis at higher temperatures (up to 200 K) in the case of LTA sample as compared to the HTA sample clearly unveil different magnetic states associated with them.