Microstructure evolution of AZ31 magnesium alloy during warm compression forming

被引：0

作者：

Zhang, Z. M. ^{[1
]}

Wang, Q. ^{[1
]}

Li, B. C. ^{[1
]}

Zhang, X. ^{[2
]}

机构：

[1] North Univ China, Dept Mat Sci & Engn, Taiyuan 030051, Peoples R China

[2] Engn Technol Res Ctr Integrated Precis Forming, Taiyuan 030051, Peoples R China

来源：

THERMEC 2006, PTS 1-5 | 2007年 / 539-543卷

关键词：

magnesium alloy; AZ31; warm forming; recrystallization;

D O I：

10.4028/www.scientific.net/MSF.539-543.1813

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

Warm compression tests of AZ31 Mg alloy were carried out at five temperatures in 30 degrees C intervals from 210 degrees C to 330 degrees C. The samples of different thickness which were machined from as-cast and pre-strained AZ31 billets were compressed into thickness I mm and then cooled in the air to room temperature. The microstructural evolution of AZ31 Mg alloy was investigated during warm compression forming. The results show that all the samples have undergone a microstructure changes to different scales in the range investigated. The twinning is the predominant deformation mechanism for magnesium alloys at moderate temperatures and its occurrence is dependent on temperature and strain. Microstructural evaluation indicates that the mean size of the recrystallised grains decreases with increasing effective strain and temperature because of sufficient dynamic recrystallization. The original grain has significant influence on microstructural evolution during warm forming.

引用

页码：1813 / +

页数：2

共 13 条

[11] Mechanical properties of Mg-Y-Zn alloy processed by equal-channel-angular extrusion [J].

Watanabe, H ;

Mukai, T ;

Kamado, S ;

Kojima, Y ;

Higashi, K .

MATERIALS TRANSACTIONS, 2003, 44 (04) :463-467

[12] Realization of high strength and high ductility for AZ61 magnesium alloy by severe warm working [J].

Yoshida, Y ;

Arai, K ;

Itoh, S ;

Kamado, S ;

Kojima, Y .

SCIENCE AND TECHNOLOGY OF ADVANCED MATERIALS, 2005, 6 (02) :185-194

[13] Strengthening behaviours of AZ31 Mg-alloy during warm forming [J].

Zhang, ZM ;

Wang, Q ;

Zhang, BH .

MAGNESIUM - SCIENCE, TECHNOLOGY AND APPLICATIONS, 2005, 488-489 :539-542

← 1 2 →