The effect of thickness on the creep properties of a single-crystal nickel-based superalloy

被引：46

作者：

Hu, Yebing ^{[1
]}

Zhang, Li ^{[2
]}

Cao, Tieshan ^{[1
]}

Cheng, Congqian ^{[1
]}

Zhao, Pengtao ^{[2
]}

Guo, Guangping ^{[2
]}

Zhao, Jie ^{[1
]}

机构：

[1] Dalian Univ Technol, Sch Mat Sci & Engn, 2 Linggong Rd, Dalian 116024, Peoples R China

[2] Beijing Inst Aeronaut Mat, Beijing 100095, Peoples R China

来源：

MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING | 2018年 / 728卷

基金：

中国国家自然科学基金;

关键词：

Creep; Single crystal; Oxidation; Internal nitrides; Voids; Crack; OXIDATION; BEHAVIOR; MECHANISM; DD6;

D O I：

10.1016/j.msea.2018.04.114

中图分类号：

TB3 [工程材料学];

学科分类号：

0805 ; 080502 ;

摘要：

Creep rupture tests were conducted at 980 degrees C/250 MPa on specimens with different wall thickness values obtained from a single-crystal nickel-based superalloy. Experimental results showed that the thin specimens had an inferior creep life compared with the thick ones. All specimens were oxidised during the creep tests. Electron probe microanalysis and scanning electron microscopy combined with energy-dispersive X-ray spectroscopy revealed that internal nitrides developed in the y'-free zone and even in the matrix. The presence of internal nitrides induced the nucleation of creep voids and initiation of cracks during creep rupture, thereby increasing the growth rate of cracks and facilitating the failure of the creep specimens. The morphology of the fracture sections indicated that the interaction of cracks and creep damage also contributed to this phenomenon. Cracks played an important role in the creep behaviour of the thin specimens, and creep damage effectively influenced that of the thick specimens.

引用

页码：124 / 132

页数：9

共 32 条

[1] Influence of oxidation on near-surface γ′ fraction and resulting creep behaviour of single crystal Ni-base superalloy M247LC SX [J].

Bensch, M. ;

Konrad, C. H. ;

Fleischmann, E. ;

Rae, C. M. F. ;

Glatzel, U. .

MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2013, 577 :179-188

[2] Modelling and analysis of the oxidation influence on creep behaviour of thin-walled structures of the single-crystal nickel-base superalloy Rene N5 at 980 °C [J].

Bensch, Matthias ;

Preussner, Johannes ;

Huettner, Rainer ;

Obigodi, Georgia ;

Virtanen, Sannakaisa ;

Gabel, Johannes ;

Glatzel, Uwe .

ACTA MATERIALIA, 2010, 58 (05) :1607-1617

[3]

Bullock E., 2012, Research and Development of High Temperature Materials for Industry

[4] The effect of thickness on the creep response of thin-wall single crystal components [J].

Cassenti, Brice ;

Staroselsky, Alexander .

MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2009, 508 (1-2) :183-189

[5] The role of oxidation damage in fatigue crack initiation of an advanced Ni-based superalloy [J].

Cruchley, S. ;

Li, H. Y. ;

Evans, H. E. ;

Bowen, P. ;

Child, D. J. ;

Hardy, M. C. .

INTERNATIONAL JOURNAL OF FATIGUE, 2015, 81 :265-274

[6] Static and dynamic aspects of coupling between creep behavior and oxidation on MC2 single crystal superalloy at 1150 °C [J].

Dryepondt, S ;

Monceau, D ;

Crabos, F ;

Andrieu, E .

ACTA MATERIALIA, 2005, 53 (15) :4199-4209

[7] Mechanisms of high-temperature creep of nickel-based superalloys under low applied stresses [J].

Epishin, A ;

Link, T .

PHILOSOPHICAL MAGAZINE, 2004, 84 (19) :1979-2000

[8]

EVANS HE, 1995, INT MATER REV, V40, P1, DOI 10.1179/095066095790151124

[9] Corrosion kinetics of a directionally solidified Ni-base superalloy [J].

Gordon, Ali P. ;

Trexler, Matthew D. ;

Neu, Richard W. ;

Sanders, Thomas J. ;

McDowell, David L. .

ACTA MATERIALIA, 2007, 55 (10) :3375-3385

[10]

Hardy M., P SUP 2016 13 INT S, P653

← 1 2 3 4 →