Economical and Efficient Protection for Blast Furnace Hearth

被引：29

作者：

Deng, Yong ^{[1
,2
]}

Zhang, Jian-liang ^{[1
,2
]}

Jiao, Ke-xin ^{[1
,2
]}

机构：

[1] Univ Sci & Technol Beijing, Sch Met & Ecol Engn, Beijing 100083, Peoples R China

[2] Univ Sci & Technol Beijing, State Key Lab Adv Met, Beijing 100083, Peoples R China

来源：

ISIJ INTERNATIONAL | 2018年 / 58卷 / 07期

基金：

美国国家科学基金会;

关键词：

blast furnace; economical and efficient protection; carbon undersaturation degree; economic evaluation; fettling rate; TIO2; SLAG; THERMODYNAMICS; VISCOSITY; TITANIUM; BASICITY;

D O I：

10.2355/isijinternational.ISIJINT-2018-005

中图分类号：

TF [冶金工业];

学科分类号：

0806 ;

摘要：

In order to clarify the erosion mechanism of carbon brick and realize the economical and efficient protection for blast furnace hearth at the end of the service. The damaged carbon bricks were sampled from a commercial blast furnace, the microstructure of the damaged carbon bricks was analyzed through SEM and EDS. The carbon undersaturation degrees of molten iron for different volume blast furnace were calculated, the dissolution and the penetration were considered as the reasons for the erosion of carbon brick. A model of economical and efficient protection for hearth was established based on various factors, the economy of protection raw material and the protection effect can be evaluated through the model. The model guides the selection of the economical protection raw material according to the evaluation, the reasonable operation can be obtained according to the calculation of the fettling rate.

引用

页码：1198 / 1203

页数：6

共 20 条

[1] Crack generation in blast furnace slag bearing high titanium by microwave cyclic heating [J].

Chen, Yan ;

Ishizuka, Etsuko ;

Yoshikawa, Noboru ;

Taniguchi, Shoji .

ISIJ INTERNATIONAL, 2007, 47 (02) :193-196

[2] Nanoporous TiO2 film electrode for electrocatalytic reduction of 2-pyridineethanol in ionic liquids [J].

Chu, Daobao ;

Qin, Guoxu ;

Yuan, Ximei ;

Xu, Mai ;

Lu, Jia ;

Zheng, Peng .

JOURNAL OF POROUS MATERIALS, 2008, 15 (06) :661-665

[3] Microstructure and mechanical property in a high strength high-Al-low-Si hot-dip galvanized dual phase steel [J].

Deng, Yonggang ;

Di, Hongshuang ;

Hu, Meiyuan ;

Zhang, Jiecen ;

Misra, R. D. K. .

METALLURGICAL RESEARCH & TECHNOLOGY, 2017, 114 (02)

[4] Effects of Temperature, Refractory Composition and Mass Transfer Rate on Corrosion Rate of Al2O3-SiO2 System Bricks into CaO-SiO2-Al2O3-MgO Slag [J].

Hino, Yuta ;

Matsunaga, Hisahiro ;

Watanabe, Keiji .

ISIJ INTERNATIONAL, 2017, 57 (04) :697-705

[5] Analysis of Blast Furnace Hearth Sidewall Erosion and Protective Layer Formation [J].

Jiao, Ke-Xin ;

Zhang, Jian-Liang ;

Liu, Zheng-Jian ;

Chen, Chun-Lin ;

Liu, Yan-Xiang .

ISIJ INTERNATIONAL, 2016, 56 (11) :1956-1963

[6]

Jin Y, 2009, J IRON STEEL RES INT, V16, P902

[7] Influence of Basicity and TiO2 Content on the Precipitation Behavior of the Ti-bearing Blast Furnace Slags [J].

Li, Jing ;

Zhang, Zuotai ;

Liu, Lili ;

Wang, Wanlin ;

Wang, Xidong .

ISIJ INTERNATIONAL, 2013, 53 (10) :1696-1703

[8] Thermodynamics of TiCN and TiC in Fe-Csat melts [J].

Li, Y ;

Fruehan, RJ .

METALLURGICAL AND MATERIALS TRANSACTIONS B-PROCESS METALLURGY AND MATERIALS PROCESSING SCIENCE, 2001, 32 (06) :1203-1205

[9] Influence of TiO2 and basicity on viscosity of Ti bearing slag [J].

Liao, J. L. ;

Li, J. ;

Wang, X. D. ;

Zhang, Z. T. .

IRONMAKING & STEELMAKING, 2012, 39 (02) :133-139

[10] Low Carbon Operation of Super-Large Blast Furnaces in China [J].

Liu, Zheng-jian ;

Zhang, Jian-liang ;

Yang, Tian-jun .

ISIJ INTERNATIONAL, 2015, 55 (06) :1146-1156

← 1 2 →