Temperature dependent deformation behavior and stacking fault energy of Fe40Mn40Co10Cr10 alloy

被引：53
作者：
Chandan, A. K. [1 ,2 ]
Tripathy, S. [1 ,2 ]
Sen, B. [3 ]
Ghosh, M. [1 ,2 ]
Chowdhury, S. Ghosh [1 ,2 ]
机构：
[1] Acad Sci & Innovat Res AcSIR, Ghaziabad 201002, India
[2] CSIR Natl Met Lab, Mat Engn Div, Jamshedpur 831007, Bihar, India
[3] Natl Inst Technol, Dept Met & Mat Engn, Rourkela 769008, India
来源：
SCRIPTA MATERIALIA | 2021年 / 199卷
关键词：
High entropy alloy; Stacking fault energy; Nano-twins; Martensitic transformation; HIGH-ENTROPY ALLOY; MECHANICAL-PROPERTIES; PHASE-TRANSFORMATION; MN; STRENGTH; STEELS; AL; CO; EVOLUTION; DESIGN;
D O I：
10.1016/j.scriptamat.2021.113891
中图分类号：
TB3 [工程材料学];
学科分类号：
0805 ; 080502 ;
摘要：
The variation in stacking fault energy (SFE) with the change in temperature has been evaluated experimentally for Fe40Mn40Co10Cr10 high entropy alloy. The distance between partial dislocations was measured using transmission electron microscopy (TEM) based weak-beam dark field (WBDF) technique. SFE of the system was found to be 37.7 (+/- 7) mJ/m(2) and 19.5 (+/- 5) mJ/m(2) at room temperature (RT) and -100 degrees C, respectively. Owing to the decrease in SFE, a transition in the deformation behavior occurred from limited twin formation and slip dominance at RT to mixed-mode consisting of FCC -> HCP transformation and twinning at -100 degrees C. Simultaneous occurrence of twins and deformation-induced martensitic transformation led to superior strength-ductility combination in the specimen deformed at -100 degrees C. SFE of the studied alloy at RT was 42% higher than that of the equiatomic FeMnCoCrNi alloy. This increase in SFE, despite removal of Ni can be understood by considering the effect of the alloy chemistry re-adjustment on Delta G(gamma ->epsilon). (C) 2021 Acta Materialia Inc. Published by Elsevier Ltd. All rights reserved.
引用
收藏
页数：5
相关论文
共 38 条
[1]   Correlations between the calculated stacking fault energy and the plasticity mechanisms in Fe-Mn-C alloys [J].
Allain, S ;
Chateau, JP ;
Bouaziz, O ;
Migot, S ;
Guelton, N .
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2004, 387 :158-162
[2]   Exceptional phase-transformation strengthening of ferrous medium entropy alloys at cryogenic temperatures [J].
Bae, Jae Wung ;
Seol, Jae Bok ;
Moon, Jongun ;
Sohn, Seok Su ;
Jang, Min Ji ;
Um, Ho Yong ;
Lee, Byeong-Joo ;
Kim, Hyoung Seop .
ACTA MATERIALIA, 2018, 161 :388-399
[3]   Significance of interplay between austenite stability and deformation mechanisms in governing three-stage work hardening behavior of phase-reversion induced nanograined/ultrafine-grained (NG/UFG) stainless steels with high strength-high ductility combination [J].
Challa, V. S. A. ;
Wan, X. L. ;
Somani, M. C. ;
Karjalainen, L. P. ;
Misra, R. D. K. .
SCRIPTA MATERIALIA, 2014, 86 :60-63
[4]   Evolution of Substructure of a Non-equiatomic FeMnCrCo High Entropy Alloy Deformed at Ambient Temperature [J].
Chandan, A. K. ;
Tripathy, S. ;
Ghosh, M. ;
Chowdhury, S. G. .
METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 2019, 50A (11) :5079-5090
[5]  
COCKAYNE DJ, 1972, Z NATURFORSCH PT A, VA 27, P452
[6]   Design of a twinning-induced plasticity high entropy alloy [J].
Deng, Y. ;
Tasan, C. C. ;
Pradeep, K. G. ;
Springer, H. ;
Kostka, A. ;
Raabe, D. .
ACTA MATERIALIA, 2015, 94 :124-133
[7]  
GALLAGHER PC, 1970, METALL TRANS, V1, P2429
[8]   Exceptional damage-tolerance of a medium-entropy alloy CrCoNi at cryogenic temperatures [J].
Gludovatz, Bernd ;
Hohenwarter, Anton ;
Thurston, Keli V. S. ;
Bei, Hongbin ;
Wu, Zhenggang ;
George, Easo P. ;
Ritchie, Robert O. .
NATURE COMMUNICATIONS, 2016, 7
[9]   A fracture-resistant high-entropy alloy for cryogenic applications [J].
Gludovatz, Bernd ;
Hohenwarter, Anton ;
Catoor, Dhiraj ;
Chang, Edwin H. ;
George, Easo P. ;
Ritchie, Robert O. .
SCIENCE, 2014, 345 (6201) :1153-1158
[10]   High strength Fe-Mn-(Al, Si) TRIP/TWIP steels development -: properties -: application [J].
Grässel, O ;
Krüger, L ;
Frommeyer, G ;
Meyer, LW .
INTERNATIONAL JOURNAL OF PLASTICITY, 2000, 16 (10-11) :1391-1409
1234