The rim cracking of railway wheels and the fatigue resistance of the steels used

被引：0
|
作者：
Zhou, ZY [1 ]
Yun, JS [1 ]
Xia, LZ [1 ]
Cheng, GH [1 ]
机构：
[1] Maanshan Iron & Steel Co, Iron & Steel Res Inst, An Hui, Peoples R China
来源：
PROGRESS IN MECHANICAL BEHAVIOUR OF MATERIALS (ICM8), VOL 1: FATIGUE AND FRACTURE | 1999年
关键词：
D O I：
暂无
中图分类号：
TH [机械、仪表工业];
学科分类号：
0802 ;
摘要：
Rim cracking is the most dangerous failure mode of railway carwheel. The crack is nucleated interior the rim below the tread surface about 5-25mm. In order to prevent the rim cracking, four kinds of steels with different carbon content have been investigated. The mechanical behaviors and microstructures of the steels are analysed.
引用
收藏
页码：332 / 337
页数：4
相关论文
共 50 条
  • [41] Thermomechanical fatigue fracture due to repeated braking of railway wheels
    Rossmanith, H. P.
    Loibnegger, F.
    Huber, R.
    MATERIALS SCIENCE, 2006, 42 (04) : 466 - 475
  • [42] Influence of the steel grades on rolling contact fatigue of railway wheels
    Langueh, A.
    Brunel, J-F.
    Charkaluk, E.
    Dufrenoy, P.
    Demilly, F.
    11TH INTERNATIONAL CONFERENCE ON THE MECHANICAL BEHAVIOR OF MATERIALS (ICM11), 2011, 10
  • [43] CARBIDE STEELS WITH INCREASED CRACKING RESISTANCE
    MASLENNIKOV, NN
    LATYPOV, MG
    SHATSOV, AA
    METAL SCIENCE AND HEAT TREATMENT, 1993, 35 (7-8) : 455 - 459
  • [44] Technological provision of contact fatigue resistance for cemented gear wheels made of heat-resistant steels
    N. M. Ryzhov
    Metal Science and Heat Treatment, 2010, 52 : 330 - 335
  • [45] TECHNOLOGICAL PROVISION OF CONTACT FATIGUE RESISTANCE FOR CEMENTED GEAR WHEELS MADE OF HEAT-RESISTANT STEELS
    Ryzhov, N. M.
    METAL SCIENCE AND HEAT TREATMENT, 2010, 52 (7-8) : 330 - 335
  • [46] CRACKING RESISTANCE AND STRENGTH OF CARBIDE STEELS
    KYUBARSEPP, YP
    ANNUKA, KI
    RESHETNYAK, KD
    MAISTRENKO, AL
    CHEPOVETSKII, GI
    SOVIET POWDER METALLURGY AND METAL CERAMICS, 1990, 29 (01): : 83 - 87
  • [47] Fatigue damage mechanism of railway wheels under lateral forces
    Zhou, Guiyuan
    He, Chenggang
    Wen, Guang
    Liu, Qiyue
    TRIBOLOGY INTERNATIONAL, 2015, 91 : 160 - 169
  • [48] Heat Treatment of UIC Quality Compact Railway Wheels with Water Sprayed Rim.
    Mitura, Karel
    Faja, Rudolf
    Balcarek, Vilem
    Cupita, Frantisek
    Hutnicke listy, 1988, 43 (01): : 25 - 32
  • [49] Limiting Factors for Choice and Development of Steels for Railway Wheels and Rails.
    Masin, Alois
    Hutnicke listy, 1984, 39 (08): : 552 - 559
  • [50] INHIBITING THE STRESS-CORROSION CRACKING OF STEELS AND CORROSION FATIGUE OF STEELS
    RATYCH, LV
    SLOBODYAN, IM
    PROTECTION OF METALS, 1989, 25 (05): : 575 - 580
12345