The rim cracking of railway wheels and the fatigue resistance of the steels used

被引：0
|
作者：
Zhou, ZY [1 ]
Yun, JS [1 ]
Xia, LZ [1 ]
Cheng, GH [1 ]
机构：
[1] Maanshan Iron & Steel Co, Iron & Steel Res Inst, An Hui, Peoples R China
来源：
PROGRESS IN MECHANICAL BEHAVIOUR OF MATERIALS (ICM8), VOL 1: FATIGUE AND FRACTURE | 1999年
关键词：
D O I：
暂无
中图分类号：
TH [机械、仪表工业];
学科分类号：
0802 ;
摘要：
Rim cracking is the most dangerous failure mode of railway carwheel. The crack is nucleated interior the rim below the tread surface about 5-25mm. In order to prevent the rim cracking, four kinds of steels with different carbon content have been investigated. The mechanical behaviors and microstructures of the steels are analysed.
引用
收藏
页码：332 / 337
页数：4
相关论文
共 50 条
  • [1] Study on damage tolerance and remain fatigue life of shattered rim of railway wheels
    Cong, Tao
    Liu, Xiaolong
    Wu, Si
    Zhang, Guanzhen
    Chen, Erqing
    Qian, Guian
    Berto, Filippo
    ENGINEERING FAILURE ANALYSIS, 2021, 123
  • [2] Modelling shattered rim cracking in railroad wheels
    Sura, V.
    Mahadevan, S.
    PROCEEDINGS OF THE INSTITUTION OF MECHANICAL ENGINEERS PART F-JOURNAL OF RAIL AND RAPID TRANSIT, 2011, 225 (F6) : 593 - 604
  • [3] Cyclic deformation and fatigue behaviour of microalloyed carbon steels for use in railway wheels
    Ahlström, J
    Karlsson, B
    ADVANCES IN MECHANICAL BEHAVIOUR, PLASTICITY AND DAMAGE, VOLS 1 AND 2, PROCEEDINGS, 2000, : 1021 - 1026
  • [4] Resistance of steels of railroad wheels to corrosion-fatigue fracture
    I. M. Andreiko
    V. V. Kulyk
    O. P. Ostash
    Materials Science, 2012, 47 : 608 - 612
  • [5] Resistance of steels of railroad wheels to corrosion-fatigue fracture
    Andreiko, I. M.
    Kulyk, V. V.
    Ostash, O. P.
    MATERIALS SCIENCE, 2012, 47 (05) : 608 - 612
  • [6] Fatigue behaviour of two microalloyed steels used in automotive wheels discs
    Rabbi, M
    Bastian, F
    Martins, C
    Gritti, J
    Godefroid, L
    FATIGUE '99: PROCEEDINGS OF THE SEVENTH INTERNATIONAL FATIGUE CONGRESS, VOLS 1-4, 1999, : 2647 - 2652
  • [7] Modeling of vertical split rim cracking in railroad wheels
    Sura, Venkata
    Mahadevan, Sankaran
    ENGINEERING FAILURE ANALYSIS, 2011, 18 (04) : 1171 - 1183
  • [8] Determination of the Threshold for the Development of Fatigue Cracks in Steels Used in Railway Structures
    Moskvitin, G. V.
    Lebedinskii, S. G.
    JOURNAL OF MACHINERY MANUFACTURE AND RELIABILITY, 2007, 36 (06): : 554 - 558
  • [9] Determination of the threshold for the development of fatigue cracks in steels used in railway structures
    G. V. Moskvitin
    S. G. Lebedinskii
    Journal of Machinery Manufacture and Reliability, 2007, 36 (6) : 554 - 558
  • [10] Fatigue durability of steels of railroad wheels
    O. P. Ostash
    I. M. Andreiko
    V. V. Kulyk
    I. H. Uzlov
    O. I. Babachenko
    Materials Science, 2007, 43 : 403 - 414
12345