Investigations of the non-isothermal crystallization of CaF2 nanoparticles in Sm-doped oxy-fluoride glasses

Oxyfluoride glass samples in the system SiO2-Al2O3-CaF2-SmF3 were produced by using the melt-quenched technique and the kinetics of non-isothermal crystallization of CaF2 nano-crystals has been investigated. Differential thermal analysis (DTA) has shown an exothermic peak at about 700 degrees C which was assigned to the CaF2 nano-crystals precipitation within the glass matrix as was identified by X-ray diffraction (XRD) analysis of the annealed glass samples. It was shown the Ozawa model is most suitable for describing the behaviour of non-isothermal crystallization of CaF2 nano-crystals within the glass matrix. The mean value of the Avrami exponent was found 1.16 which indicates the diffusion-controlled growth process of nano-particles in the glass system with zero nucleation rate as the single operative mechanism; the activation energy of the crystallization is E-d = 379 +/- 25 kJ/mol (3.93 +/- 0.26 eV). The activation energy of the nano-crystals growth was computed within the same model and agrees very well with the activation energy of the crystallization. (C) 2010 Elsevier B.V. All rights reserved.