The role of neodymium based thin film on the epoxy/steel interfacial adhesion and corrosion protection promotion

被引：64
作者：
Majd, Mehdi Tabatabaei [1 ]
Shahrabi, Taghi [1 ]
Ramezanzadeh, Bahram [2 ]
机构：
[1] Tarbiat Modares Univ, Dept Mat Engn, Fac Engn, POB 14115-143, Tehran, Iran
[2] ICST, Dept Surface Coatings & Corros, PO 16765-654, Tehran, Iran
来源：
APPLIED SURFACE SCIENCE | 2019年 / 464卷
关键词：
Nd-based film; Corrosion; EIS; XPS; AFM; FE-SEM; AZ31 MAGNESIUM ALLOY; CERIUM CONVERSION COATINGS; ZINC PHOSPHATE; ELECTROCHEMICAL IMPEDANCE; CATHODIC DELAMINATION; COATED STEEL; CARBON-STEEL; PERFORMANCE; MECHANISM; DEPOSITION;
D O I：
10.1016/j.apsusc.2018.09.109
中图分类号：
O64 [物理化学（理论化学）、化学物理学];
学科分类号：
070304 ; 081704 ;
摘要：
The main aim of this study is to investigate the impact of the steel substrate Nd-based chemical modification on the corrosion protection performance, cathodic delamination and adhesion properties of epoxy coating. The morphology, chemical composition, topography and chemistry of the treated samples were studied by field emission scanning electron microscopy (FE-SEM), X-ray photoelectron spectroscopy (XPS), atomic force microscopy (AFM) and contact angle measurement. The treated samples and also the epoxy coated samples corrosion resistance was examined through electrochemical impedance spectroscopy (EIS). The impact of mild steel surface modification on the epoxy coating protection efficiency, adhesion strength and cathodic disbondment (CD) resistance was surveyed by salt spray, Pull-off and CD tests. Results showed the deposition of Nd oxide/hydroxide, a surface with lower surface free energy and higher roughness compared to the untreated sample. Chemical treatment by Nd-based film remarkably improved the epoxy coating corrosion protection properties, increased the adhesion strength through chemical and hydrogen bonds, and led to an excellent CD resistance.
引用
收藏
页码：516 / 533
页数：18
相关论文
共 60 条
[1]   Studies of the formation of cerium-rich protective films using x-ray absorption near-edge spectroscopy and rotating disk electrode methods [J].
Aldykiewicz, AJ ;
Davenport, AJ ;
Isaacs, HS .
JOURNAL OF THE ELECTROCHEMICAL SOCIETY, 1996, 143 (01) :147-154
[2]   In-Situ Monitoring of Local Corrosion Process of Scratched Epoxy Coated Carbon Steel in Simulated Pore Solution Containing Varying percentage of Chloride ions by Localized Electrochemical Impedance Spectroscopy [J].
Balusamy, T. ;
Nishimura, T. .
ELECTROCHIMICA ACTA, 2016, 199 :305-313
[3]   XPS characterization and corrosion resistance of cerium-treated magnesium coatings [J].
Ben Hassen, Samia ;
Bousselmi, Latifa ;
Bercot, Patrice ;
Rezrazi, El Mustafa ;
Triki, Ezzeddine .
RARE METALS, 2011, 30 (04) :368-373
[4]   Improvement in corrosion resistance of magnesium coating with cerium treatment [J].
Ben Hassen, Samia ;
Bousselmi, Latifa ;
Bercot, Patrice ;
Rezrazi, El Mustafa ;
Triki, Ezzeddine .
RARE METALS, 2009, 28 (03) :277-283
[5]   Kinetic and mechanistic studies of rare earth-rich protective film formation using in situ ellipsometry [J].
Böhm, S ;
Greef, R ;
McMurray, HN ;
Powell, SM ;
Worsley, DA .
JOURNAL OF THE ELECTROCHEMICAL SOCIETY, 2000, 147 (09) :3286-3293
[6]   Formation of a cerium-based conversion coating on AA2024: relationship with the microstructure [J].
Campestrini, P ;
Terryn, H ;
Hovestad, A ;
de Wit, JHW .
SURFACE & COATINGS TECHNOLOGY, 2004, 176 (03) :365-381
[7]   Photo-assisted reduction in nanostructured cerium-based coatings [J].
Castano, Carlos E. ;
O'Keefe, Matthew J. ;
Fahrenholtz, William G. .
SCRIPTA MATERIALIA, 2013, 69 (06) :489-492
[8]   The role of phosphorus in the eutrophication of receiving waters: A review [J].
Correll, DL .
JOURNAL OF ENVIRONMENTAL QUALITY, 1998, 27 (02) :261-266
[9]  
COTTER J, 1974, INT METALL REV, V19, P103
[10]   Study of gadolinium based protective coating for magnesium alloys [J].
Cui, X. F. ;
Jin, G. ;
Yang, Y. Y. ;
Lin, L. L. ;
Wang, H. D. ;
Xu, B. S. .
SURFACE ENGINEERING, 2012, 28 (10) :719-724
123456