The intergranular oxidation behavior of low-angle grain boundary of alloy 600 in simulated pressurized water reactor primary water

被引：34
作者：
Feng, Xingyu [1 ]
Xie, Jiayu [1 ]
Huang, Mingzheng [1 ]
Kuang, Wenjun [1 ]
机构：
[1] Xi An Jiao Tong Univ, Ctr Adv Mat Performance Nanoscale CAMP Nano, State Key Lab Mech Behav Mat, Xian 710049, Peoples R China
来源：
ACTA MATERIALIA | 2022年 / 224卷
基金：
中国国家自然科学基金;
关键词：
Alloy; 600; STEM; Grain boundary diffusion; Grain boundary migration; Intergranular oxidation; STRESS-CORROSION CRACKING; QUANTITATIVE ASSESSMENT; SECONDARY-SIDE; HIGH-TEMPERATURE; MIGRATION; DIFFUSION; CHARACTER; STEAM; SUBMODES; ORIENTATION;
D O I：
10.1016/j.actamat.2021.117533
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
The preferential intergranular oxidation (PIO) behavior of low-angle grain boundaries (LAGBs) with misorientation angle 0 ranging from 5.7 to 14.0 degrees on alloy 600 were investigated after exposure to simulated pressurized water reactor primary water. Interestingly, all LAGBs are susceptible to PIO. When 0 < 8.8 degrees, diffusion-induced grain boundary migration (DIGM) does not occur as Cr is immobile and the PIO depth varies slightly among those LAGBs. As 0 increases above 8.8 degrees, Cr starts to diffuse outwards and DIGM occurs. The depths of PIO and DIGM are positively correlated in this case. Also, the PIO depth is not related to the change of 0, but instead poses an inverse relationship with the atom packing density of GB planes. (c) 2021 Acta Materialia Inc. Published by Elsevier Ltd. All rights reserved.
引用
收藏
页数：12
相关论文
共 50 条
[31]   Deformation band corrosion as a result of applied stress and cold-work in 304 stainless steel in simulated pressurized water reactor primary water conditions [J].
Kruska, Karen ;
Saxey, David W. ;
Terachi, Takumi ;
Yamada, Takuyo ;
Schreiber, Daniel K. ;
Lozano-Perez, Sergio .
JOURNAL OF NUCLEAR MATERIALS, 2025, 607
[32]   Replicating PWR Primary Water Conditions in Low Pressure H2-Steam Environment to Study Alloy 600 Oxidation Processes [J].
Volpe, L. ;
Bertali, G. ;
Curioni, M. ;
Burke, M. G. ;
Scenini, F. .
JOURNAL OF THE ELECTROCHEMICAL SOCIETY, 2019, 166 (02) :C1-C8
[33]   Understanding the role of Diffusion Induced Grain Boundary Migration on the preferential intergranular oxidation behaviour of Alloy 600 via advanced microstructural characterization [J].
Volpe, L. ;
Burke, M. G. ;
Scenini, F. .
ACTA MATERIALIA, 2019, 175 :238-249
[34]   The Characteristics of the Oxide Films Formed on Ni-base Alloy Cladding in Simulated Pressurized Water Reactor Primary Water Environment [J].
Jia, Yibo ;
Ling, Sichun ;
Zhang, Kun ;
Ma, Jiarong ;
Cui, Tongming ;
Xiong, Qi ;
Lu, Zhanpeng ;
Li, Shuangyan ;
Zhang, Maolong .
SELECTED PROCEEDINGS FROM THE 233RD ECS MEETING, 2018, 85 (13) :625-634
[35]   Micro-mechanical measurement of fracture behaviour of individual grain boundaries in Ni alloy 600 exposed to a pressurized water reactor environment [J].
Stratulat, Alisa ;
Armstrong, David E. J. ;
Roberts, Steve G. .
CORROSION SCIENCE, 2016, 104 :9-16
[36]   Assessing the influence of welding-induced mechanics on oxidation and stress corrosion cracking in an Alloy 600-Alloy 152 M weldment under simulated PWR primary water [J].
Xu, Xinhe ;
Pan, Deng ;
Li, Entong ;
Lu, Zhanpeng ;
Cui, Tongming ;
Chen, Junjie ;
Zheng, Hui ;
Li, Kai ;
Lozano-Perez, Sergio ;
Shoji, Tetsuo .
JOURNAL OF NUCLEAR MATERIALS, 2024, 601
[37]   Effects of Matrix and Dendrite Boundary Composition on Stress Corrosion Cracking Performance of Alloy 52M Buttering Layer in Simulated Pressurized Water Reactor Primary Water [J].
Ma, Jiarong ;
Xiong, Qi ;
Xu, Xinhe ;
Cui, Tongming ;
Lu, Zhanpeng ;
Shoji, Tetsuo .
CORROSION, 2024, 80 (01) :69-84
[38]   The correlation between the dislocation slip/grain boundary interaction mode and the resistance to SCC initiation of Alloy 690 in simulated PWR primary water [J].
Kuang, Wenjun ;
Ning, Zehao ;
Yue, Han ;
Hao, Xianchao ;
Li, Jiang .
CORROSION SCIENCE, 2023, 217
[39]   Quantitatively evaluating the contribution of intergranular carbides, Cr-depleted zone, and grain boundary to intergranular stress corrosion cracking of Alloy 600 in a simulated boiling water reactors environment with high oxygen concentrations [J].
Liu, Pan ;
Wu, Yunlong ;
Zhong, Xiangyu ;
Wang, Zihao ;
Oyama, Ken ;
Ogota, Seiya ;
Watanabe, Yutaka ;
Shoji, Tetsuo .
ACTA MATERIALIA, 2024, 269
[40]   CORROSION BEHAVIOR OF NUCLEAR GRADE ALLOYS 690 AND 800 IN SIMULATED HIGH TEMPERATURE AND HIGH PRESSURE PRIMARY WATER OF PRESSURIZED WATER REACTOR [J].
Li Xiaohui ;
Wang Jianqiu ;
Han En-Hou ;
Ke Wei .
ACTA METALLURGICA SINICA, 2012, 48 (08) :941-950
12345