Macro-indentation fracture mechanisms in a super-hard hardfacing Fe-based electrode

被引：8

作者：

Bahoosh, Mohtasham ^{[1
]}

Shahverdi, Hamid Reza ^{[1
]}

Farnia, Amirreza ^{[2
]}

机构：

[1] Tarbiat Modares Univ, Dept Mat Engn, POB 14115-143, Tehran, Iran

[2] Islamic Azad Univ, Dept Mat Engn, Sci & Res Branch, Tehran, Iran

来源：

ENGINEERING FAILURE ANALYSIS | 2018年 / 92卷

关键词：

Super-hard hardfacing Fe-based electrode; Macro-indentation fracture toughness; Palmqvist crack model; Fracture mechanism; TOUGHNESS EVALUATION; ABRASIVE WEAR; MICROSTRUCTURE; ALLOYS; RESISTANCE; CARBIDES; CRACKING; NB;

D O I：

10.1016/j.engfailanal.2018.06.021

中图分类号：

TH [机械、仪表工业];

学科分类号：

0802 ;

摘要：

A super-hard hardfacing Fe-based electrode with 911 HV30 was applied to st37 substrate using flux-cored arc welding method. Microstructural study was accomplished using X-ray diffraction, scanning electron microscope and microscopic image analysis software. The fracture toughness properties of the phases were examined using the macro-indentation fracture toughness method. In the fracture toughness test, Palmqvist cracking mode was observed and the fracture toughness of the hardfacing steel was calculated to be 23.1 MPa root m. Furthermore, preferential crack growth direction, crack growth steps and the fracture behavior of the phases were determined using scanning electron microscope images.