Sol-gel processing of lead-free (Na,K)NbO3 ferroelectric films

被引：69
作者：
Lai, Fengping [1 ]
Li, Jing-Feng [1 ]
机构：
[1] Tsinghua Univ, State Key Lab New Ceram & Fine Prod, Dept Mat Sci, Beijing 100084, Peoples R China
来源：
JOURNAL OF SOL-GEL SCIENCE AND TECHNOLOGY | 2007年 / 42卷 / 03期
基金：
中国国家自然科学基金;
关键词：
sol-gel process; lead-free piezoelectric ceramic; ferroelectric; thin film; NaNbO3-KNbO3;
D O I：
10.1007/s10971-007-0741-9
中图分类号：
TQ174 [陶瓷工业]; TB3 [工程材料学];
学科分类号：
0805 ; 080502 ;
摘要：
The sol-gel processing of lead-free (Na,K) NbO3 ferroelectric films was studied. Sodium ethoxide (NaOC2H5) and potassium ethoxide (KOC2H5) were prepared by reacting solid Na and K with ethanol (99.7%) in a solvent of 2-methoxyethanol. 0.5-mu m-thick (Na,K)NbO3 thin films with orthorhombic perovskite structure were obtained by pyrolyzing at 400 degrees C and annealing at 800-900 degrees C. The films had relatively dense and uniform microstructure with grain size of about 50 nm, whose ferroelectricity was proved by the P-E hysteresis loop measurement. It was found that excess K was effective to reduce the annealing temperature for the crystallization of sol-gel-derived (Na,K)NbO3 thin films.
引用
收藏
页码：287 / 292
页数：6
相关论文
共 26 条
[1]   Electrooptic ferroelectric Na0.5K0.5NbO3 films [J].
Blomqvist, M ;
Khartsev, S ;
Grishin, A .
IEEE PHOTONICS TECHNOLOGY LETTERS, 2005, 17 (08) :1638-1640
[2]   High-performance epitaxial Na0.5K0.5NbO3 thin films by magnetron sputtering [J].
Blomqvist, M ;
Koh, JH ;
Khartsev, S ;
Grishin, A ;
Andréasson, J .
APPLIED PHYSICS LETTERS, 2002, 81 (02) :337-339
[3]   c-axis oriented (Na,K)NbO3 thin films on Si substrates using metalorganic chemical vapor deposition [J].
Cho, CR .
MATERIALS LETTERS, 2002, 57 (04) :781-786
[4]   Na0.5K0.5NbO3/SiO2/Si thin film varactor [J].
Cho, CR ;
Koh, JH ;
Grishin, A ;
Abadei, S ;
Gevorgian, S .
APPLIED PHYSICS LETTERS, 2000, 76 (13) :1761-1763
[5]   Background oxygen effects on pulsed laser deposited Na0.5K0.5NbO3 films:: From superparaelectric state to ferroelectricity [J].
Cho, CR ;
Grishin, A .
JOURNAL OF APPLIED PHYSICS, 2000, 87 (09) :4439-4448
[6]   In-plane aligned Pb(ZrxTi1-x)O3 microbelts fabricated by near migration and restricted growth [J].
Gong, W ;
Li, JF ;
Peng, CE ;
Gui, ZL ;
Li, LT .
ADVANCED MATERIALS, 2005, 17 (16) :1952-+
[7]   Single-crystal Nb-doped Pb(Zr,Ti)O3 thin films on Nb-doped SrTiO3 wafers with different orientations [J].
Gong, W ;
Li, JF ;
Chu, XC ;
Gui, ZL ;
Li, LT .
APPLIED PHYSICS LETTERS, 2004, 85 (17) :3818-3820
[8]   Effect of pyrolysis temperature on preferential orientation and electrical properties of sol-gel derived lead zirconate titanate films [J].
Gong, W ;
Li, JF ;
Chu, XC ;
Li, LT .
JOURNAL OF THE EUROPEAN CERAMIC SOCIETY, 2004, 24 (10-11) :2977-2982
[9]   Combined effect of preferential orientation and Zr/Ti atomic ratio on electrical properties of Pb(ZrxTi1-x)O3 thin films [J].
Gong, W ;
Li, JF ;
Chu, XC ;
Gui, ZL ;
Li, LT .
JOURNAL OF APPLIED PHYSICS, 2004, 96 (01) :590-595
[10]   Lead-zirconate-titanate-based piezoelectric micromachined switch [J].
Gross, SJ ;
Tadigadapa, S ;
Jackson, TN ;
Trolier-McKinstry, S ;
Zhang, QQ .
APPLIED PHYSICS LETTERS, 2003, 83 (01) :174-176
123