Synthesis and characterization of core-shell SiO2-fluorinated polyacrylate nanocomposite latex particles containing fluorine in the shell

被引：74

作者：

Cui, Xuejun ^{[1
]}

Zhong, Shuangling ^{[2
]}

Yan, Jing ^{[1
]}

Wang, Chunlei ^{[1
]}

Zhang, Haitao ^{[1
]}

Wang, Hongyan ^{[1
]}

机构：

[1] Jilin Univ, Coll Chem, Changchun 130012, Peoples R China

[2] Jilin Agr Univ, Coll Resources & Environm, Changchun 130118, Peoples R China

来源：

COLLOIDS AND SURFACES A-PHYSICOCHEMICAL AND ENGINEERING ASPECTS | 2010年 / 360卷 / 1-3期

基金：

美国国家科学基金会;

关键词：

SiO2; Fluorinated polyacrylate; Core-shell; Nanoparticles; CONTAINING COLLOIDAL DISPERSIONS; SILICA NANOPARTICLES; MORPHOLOGICAL-CHARACTERISTICS; MINIEMULSION POLYMERIZATION; EMULSION POLYMERIZATION; INORGANIC PARTICLES; BLOCK-COPOLYMERS; FILM FORMATION; HYBRID; POLYSTYRENE;

D O I：

10.1016/j.colsurfa.2010.02.006

中图分类号：

O64 [物理化学（理论化学）、化学物理学];

学科分类号：

070304 ; 081704 ;

摘要：

The core-shell SiO2-fluorinated polyacrylate nanocomposite latex particles containing fluorine in the shell were successfully synthesized by seeded emulsion polymerization with nano-SiO2 as seeds Transmission election microscopy (TEM) confirmed that the resultant particles had the core-shell structure obviously Scanning electron microscopy (SEM), TEM and dynamic light scattering (DLS) analysis indicated that the obtained core-shell nanocomposite latex particles were uniform and possessed narrow size distributions The chemical components of the core-shell nanocomposite latex particles were investigated by Fourier transform infrared (MR) spectrometry and X-ray photoelectron spectroscopy (XPS) analysis, respectively. XPS analysis of the SiO2-fluorinated polyacrylate nanocomposite latex films revealed that the intensity of fluorine signal in the film-air interface is higher than that in the film-glass interface In addition. compared with the film of core-shell SiO2-polyacrylate nanocomposite latex prepared under the similar polymerization condition, the core-shell SiO2-fluorinated polyacrylate nanocomposite latex film showed higher contact angle and thermal stability (C) 2010 Elsevier B.V. All rights reserved

引用

页码：41 / 46

页数：6

共 48 条

[41] Low-surface-energy fluoromethacrylate block copolymers with patternable elements [J].

Yang, S ;

Wang, JG ;

Ogino, K ;

Valiyaveettil, S ;

Ober, CK .

CHEMISTRY OF MATERIALS, 2000, 12 (01) :33-40

[42]

Zhang CC, 2005, POLYM INT, V54, P1027, DOI [10.1002/pi.1803, 10.1002/pi.l803]

[43] Preparation of styrene-acrylic emulsion by using nano-SiO2 as seeds [J].

Zhang, F ;

Wang, YP ;

Chai, CP .

POLYMER INTERNATIONAL, 2004, 53 (09) :1353-1359

[44] Monodisperse silica-polymer core-shell microspheres via surface grafting and emulsion polymerization [J].

Zhang, K ;

Chen, HT ;

Chen, X ;

Chen, ZM ;

Cui, ZC ;

Yang, B .

MACROMOLECULAR MATERIALS AND ENGINEERING, 2003, 288 (04) :380-385

[45] Titania-coated polystyrene hybrid microballs prepared with miniemulsion polymerization [J].

Zhang, M ;

Gao, G ;

Li, CQ ;

Liu, FQ .

LANGMUIR, 2004, 20 (04) :1420-1424

[46]

Zhong ZY, 2000, ADV MATER, V12, P206, DOI 10.1002/(SICI)1521-4095(200002)12:3<206::AID-ADMA206>3.0.CO

[47]

2-5

[48] The change of the properties of acrylic-based polyurethane via addition of nano-silica [J].

Zhou, SX ;

Wu, LM ;

Sun, J ;

Shen, WD .

PROGRESS IN ORGANIC COATINGS, 2002, 45 (01) :33-42

← 1 2 3 4 5 →