Influence of Ca ions and temperature on the corrosion behavior of WC-Co hardmetals in alkaline solutions

The effect of temperature and Ca ions on the corrosion behavior of hardmetals was investigated in 0.1 M NaOH and 0.05 M Ca(OH)(2) alkaline electrolytes using impedance spectroscopy, potentiodynamic polarization and surface analytical techniques. It was found that calcium containing alkaline solutions efficiently decrease the anodic currents up to 5 times by forming a calcium containing deposit on the top of the WC-Co hardmetal surface, which remains stable even at higher temperatures (40 degrees C and 60 degrees C). This positive influence of Ca ions is predominant under polarization in the range from 0 to +0.85 V (Ag/AgCl) but is not apparent under OCP conditions. In NaOH, however, the corrosion resistance strongly decreases at higher temperatures as compared with the room temperature. At the slightly elevated temperature in 0.1 M NaOH the Co binder phase loses its passivity and is almost completely washed out of the compound material. A WC skeleton remains on the surface and hence the ductility in the hardmetal is lost. In the end, the material could completely fail under such operating conditions. Also the Ni alloyed binder loses its strong passivation ability at the elevated temperatures. (C) 2009 Elsevier Ltd. All rights reserved.