Synthesis of Co3O4 nanorod bunches from a single precursor CO(CO3)0.35Cl0.20(OH)1.10

被引：59
|
作者：
Wang, ZH
Chen, XY
Zhang, M
Qian, YT [1 ]
机构：
[1] Univ Sci & Technol China, Struct Res Lab, Anhua 230026, Peoples R China
[2] Univ Sci & Technol China, Dept Chem, Anhua 230026, Peoples R China
来源：
SOLID STATE SCIENCES | 2005年 / 7卷 / 01期
基金：
中国国家自然科学基金;
关键词：
nanorod bunches; thermal decomposition; CO3O4; precursor;
D O I：
10.1016/j.solidstatesciences.2004.10.032
中图分类号：
O61 [无机化学];
学科分类号：
070301 ; 081704 ;
摘要：
CO3O4 nanorods were successfully synthesized from a single precursor via a thermal decomposition and oxidization route. The precursor used was Co(CO3)(0.35)Cl-0.20(OH)(1.10), which was prepared by a hydrothermal reaction using CoCl2(.)6H(2)O with CO(NH2)(2) at 95-120degreesC. Both the precursor and the as-prepared Co3O4 were characterized with XRD, TEM, SEM, TGA and XPS. The precursor, as well as CO3O4, was found to be composed of nanorods that were radially bunched. The Co3O4 nanorods obtained through a thermal treatment at 300 degreesC for 5 h were found to have a porous structure. (C) 2004 Elsevier SAS. All rights reserved.
引用
收藏
页码：13 / 15
页数：3
相关论文
共 50 条
  • [1] Vapor Phase Synthesis, Characterization and Gas Sensing Performances of Co3O4 and Au/Co3O4 Nanosystems
    Barreca, Davide
    Comini, Elisabetta
    Gasparotto, Alberto
    Maccato, Chiara
    Pozza, Andrea
    Sada, Cinzia
    Sberveglieri, Giorgio
    Tondello, Eugenio
    JOURNAL OF NANOSCIENCE AND NANOTECHNOLOGY, 2010, 10 (12) : 8054 - 8061
  • [2] Solvothermal Synthesis of CoO, Co3O4, Ni(OH)2 and Mg(OH)2 Nanotubes
    Zhuo, Linhai
    Ge, Jiechao
    Cao, Lihua
    Tang, Bo
    CRYSTAL GROWTH & DESIGN, 2009, 9 (01) : 1 - 6
  • [3] Synthesis and characterization of Co3O4 nanoparticles by a simple method
    Salavati-Niasari, Masoud
    Khansari, Afsaneh
    COMPTES RENDUS CHIMIE, 2014, 17 (04) : 352 - 358
  • [4] Synthesis and electrocatalytic performance for p-nitrophenol reduction of rod-like Co3O4 and Ag/Co3O4 composites
    Pan, Lu
    Tang, Jing
    Wang, Fengwu
    MATERIALS RESEARCH BULLETIN, 2013, 48 (07) : 2648 - 2653
  • [5] High-Yield Synthesis of Opened-Book Like Co3O4 from Precursor and Catalytic Property
    Li, Chang
    Zhang, DongEn
    Hao, XiaoYun
    Ren, LiZhen
    Xiao, Xin
    Ma, JuanJuan
    Yang, Tao
    Tong, ZhiWei
    NANOSCIENCE AND NANOTECHNOLOGY LETTERS, 2016, 8 (03) : 277 - 281
  • [6] A facile synthesis of Co3O4 nanoflakes: Magnetic and catalytic properties
    Zhang, DongEn
    Li, Feng
    Chen, AiMei
    Xie, Qing
    Wang, MingYan
    Zhang, XiaoBo
    Li, ShanZhong
    Gong, JunYan
    Han, GuiQuan
    Ying, AiLing
    Tong, ZhiWei
    SOLID STATE SCIENCES, 2011, 13 (06) : 1221 - 1225
  • [7] Facile synthesis of mesoporous Co3O4 nanowires for application in supercapacitors
    Li, Yuan
    Wu, Huijie
    Wu, Yi
    Li, Qing
    JOURNAL OF MATERIALS SCIENCE-MATERIALS IN ELECTRONICS, 2017, 28 (22) : 16826 - 16835
  • [8] Shape Controlled Synthesis and Optical Property of Co3O4 and NiO
    Zhang Ping
    Lei Chao
    Lu Zhen-Jiang
    Ji Chen-Chen
    Cai Chang-Jun
    Bao Shu-Juan
    Jia Dian-Zeng
    CHINESE JOURNAL OF INORGANIC CHEMISTRY, 2012, 28 (07) : 1435 - 1440
  • [9] Synthesis and Characterization of Co3O4 Nanoparticles by Thermal Treatment Process
    Khansari, Afsaneh
    Salavati-Niasari, Masoud
    Babaheydari, Ali Kazemi
    JOURNAL OF CLUSTER SCIENCE, 2012, 23 (02) : 557 - 565
  • [10] Synthesis of Highly Ordered Mesoporous Co3O4 for Gas Sensing
    Su, D. W.
    Liu, H.
    Ahn, H. J.
    Wang, G. X.
    JOURNAL OF NANOSCIENCE AND NANOTECHNOLOGY, 2013, 13 (05) : 3354 - 3359
12345