Dynamic fatigue of alumina

被引：2
作者：
Selverian, JH [1 ]
机构：
[1] OSRAM SYLVANIA Inc, Beverly, MA 01915 USA
来源：
JOURNAL OF MATERIALS SCIENCE | 2005年 / 40卷 / 02期
关键词：
Polymer; Alumina; Fatigue; Dynamic Fatigue;
D O I：
10.1007/s10853-005-6112-4
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
The fatigue and strength characteristics of the alumina used as lamp envelopes for high intensity discharge (HID) lamps were discussed. The alumina test samples consisted of tubes with a 3.0 mm outer diameter and 1.1 mm inner dimaeter and high purity samples were sintered above 1800 °C. The median fracture strength and other Weibull parameters at each of the stressing rate were calculated. Analysis shows that the maximum allowable stress level calculated by the fast fracture strength is significantly higher than that based on the fatigue results.
引用
收藏
页码：495 / 497
页数：3
相关论文
共 50 条
  • [11] Young’s modulus and fatigue behavior of plasma-sprayed alumina coatings
    O. Kovářík
    J. Siegl
    J. Nohava
    P. Chráska
    Journal of Thermal Spray Technology, 2005, 14 : 231 - 238
  • [12] Isothermal and thermal-mechanical fatigue of alumina
    Nejma, R
    Lang, KH
    Löhe, D
    MATERIALWISSENSCHAFT UND WERKSTOFFTECHNIK, 2005, 36 (3-4) : 136 - 139
  • [13] Static and cyclic fatigue limits of alumina ceramics
    Jin, G
    Honjoh, A
    Awaji, H
    JOURNAL OF THE CERAMIC SOCIETY OF JAPAN, 2000, 108 (06) : 614 - 616
  • [14] Fatigue wear of materials under dynamic contact loading
    Bogdanovich, P. N.
    JOURNAL OF FRICTION AND WEAR, 2013, 34 (05) : 349 - 357
  • [15] Fatigue wear of materials under dynamic contact loading
    P. N. Bogdanovich
    Journal of Friction and Wear, 2013, 34 : 349 - 357
  • [16] Characteristics of static and fatigue strength of alumina ceramic joints
    Tamai, F
    Hirano, K
    JSME INTERNATIONAL JOURNAL SERIES A-MECHANICS AND MATERIAL ENGINEERING, 1996, 39 (04): : 613 - 619
  • [17] Fatigue strength testing of LTCC and alumina ceramics bonds
    Dabrowski, A.
    Matkowski, P.
    Golonka, L.
    MATERIALS SCIENCE-POLAND, 2012, 30 (04): : 329 - 334
  • [18] Crack shielding degradation in alumina during cyclic fatigue
    El Attaoui, H
    Saâdaoui, M
    Chevalier, J
    Fantozzi, G
    EURO CERAMICS VII, PT 1-3, 2002, 206-2 : 1637 - 1640
  • [19] Fatigue degradation of the crack wake zone in monolithic alumina
    Geraghty, RD
    Hay, JC
    White, KW
    ACTA MATERIALIA, 1999, 47 (04) : 1345 - 1353
  • [20] Effect of number and size of cracks on fatigue behavior of alumina
    Yoshikawa, A
    Ikeda, K
    Kaizu, K
    Adachi, K
    PROCEEDINGS OF THE ELEVENTH (2001) INTERNATIONAL OFFSHORE AND POLAR ENGINEERING CONFERENCE, VOL IV, 2001, : 267 - 271
12345