Fatigue-Life Prediction of Corroded Steel Bar Based on Fractal Theory

被引：7

作者：

Liu, Yang ^{[1
]}

Jiang, Nan ^{[1
]}

Zhang, Haiping ^{[1
]}

Li, Ming ^{[1
]}

机构：

[1] Changsha Univ Sci & Technol, Sch Civil Engn & Architecture, Key Lab Safety Control Bridge Engn, Minist Educ & Hunan Prov, Changsha 410114, Hunan, Peoples R China

来源：

JOURNAL OF MATERIALS IN CIVIL ENGINEERING | 2018年 / 30卷 / 09期

基金：

美国国家科学基金会;

关键词：

Steel bar; Fatigue life; Fractal characteristics; Three-dimensional (3D) surface morphology coefficient; PROBABILISTIC PREDICTION; REINFORCING BARS; RC BEAMS; CORROSION; BEHAVIOR; DEGRADATION; PERFORMANCE; STRENGTH;

D O I：

10.1061/(ASCE)MT.1943-5533.0002420

中图分类号：

TU [建筑科学];

学科分类号：

0813 ;

摘要：

This paper presents an experimental study that sought to characterize the effect of corrosion and fatigue load on the behavior of reinforcing steel bars. The surface profiles of corroded steel bars and the relationship between fatigue life and corrosion morphology were investigated. First, the corrosion process was accelerated by applying external direct current. Next, fatigue tests were performed on uncorroded specimens and precorroded specimens, and the results are presented and analyzed. A method for calculating the three-dimensional (3D) corrosion morphology coefficient of corroded steel bar is proposed. The fatigue life of corroded bars is significantly reduced because of corrosion morphology, and a logarithmic linear relationship exists between fatigue life and the corrosion morphology coefficient. Considering the corrosion morphology of corroded steel bars, a method is provided to calculate the fatigue life of a corroded steel bar based on the properties of uncorroded steel bar and the 3D surface morphology coefficient of corroded steel bars. The prediction results for corroded steel bars agree well with the experimental observations.

引用

页数：11

共 26 条

[1] Mechanical behavior of corroded reinforcing steel bars S500s tempcore under low cycle fatigue [J].

Apostolopoulos, Ch. Alk. .

CONSTRUCTION AND BUILDING MATERIALS, 2007, 21 (07) :1447-1456

[2] Three-dimensional analysis of fracture, corrosion and wear surfaces [J].

Azevedo, C. R. F. ;

Marques, E. R. .

ENGINEERING FAILURE ANALYSIS, 2010, 17 (01) :286-300

[3] Cyclic behaviour of uncorroded and corroded steel reinforcing bars [J].

Caprili, Silvia ;

Salvatore, Walter .

CONSTRUCTION AND BUILDING MATERIALS, 2015, 76 :168-186

[4] Structural performance of RC beams under simultaneous loading and reinforcement corrosion [J].

Du, Yingang ;

Cullen, Martin ;

Li, Cankang .

CONSTRUCTION AND BUILDING MATERIALS, 2013, 38 :472-481

[5]

[江楠 Jiang Nan], 2016, [公路交通科技, Journal of Highway and Transportation Research and Development], V33, P66

[6] Impact of corrosion on low-cycle fatigue degradation of reinforcing bars with the effect of inelastic buckling [J].

Kashani, Mohammad M. ;

Alagheband, Peyman ;

Khan, Rafid ;

Davis, Sean .

INTERNATIONAL JOURNAL OF FATIGUE, 2015, 77 :174-185

[7] Pitting Damage Characteristics on Prestressing Steel Strands by Combined Action of Fatigue Load and Chloride Corrosion [J].

Li, Fumin ;

Luo, Xiaoya ;

Wang, Kejin ;

Ji, Yongsheng .

JOURNAL OF BRIDGE ENGINEERING, 2017, 22 (07)

[8] Fatigue behavior of naturally corroded plain reinforcing bars [J].

Li, Shibin ;

Tang, Hongwei ;

Gui, Qiang ;

Ma, Zhongguo John .

CONSTRUCTION AND BUILDING MATERIALS, 2017, 152 :933-942

[9]

[李士彬 Li Shibin], 2010, [铁道学报, Journal of the China Railway Society], V32, P93

[10]

Liu G., 2014, J BEIJING U POSTS S, V01, P12

← 1 2 3 →