Interaction of silty sand and preformed corrosion products on N80 carbon steel in CO2 environment

被引：11
|
作者：
Chen, Longjun [1 ]
Liu, Wei [1 ]
Zhang, Tianyi [1 ]
Dong, Baojun [1 ]
Li, Hai [1 ]
Sun, Yipu [1 ]
Fan, Yueming [1 ]
Zhao, Yonggang [1 ]
Li, Wenqi [1 ]
机构：
[1] Univ Sci & Technol Beijing, Inst Adv Mat & Technol, Corros & Protect Ctr, Beijing 100083, Peoples R China
来源：
CORROSION SCIENCE | 2022年 / 205卷
基金：
中国国家自然科学基金;
关键词：
Carbon steel; CO2; corrosion; Silty sand; Iron carbonate; Antagonism effect; EROSION-CORROSION; MILD-STEEL; PERFORMANCE; MECHANISM; BEHAVIOR; OIL; FILM; X65;
D O I：
10.1016/j.corsci.2022.110467
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
The interaction of silty sand and corrosion products layer in sweet environment was evaluated. Corrosion protection was a function of two factors, i.e., adsorption and embedment of silty sand, and the presence of corrosion products layer. Silty sand could block ions transportation and slow down the dissolution of FeCO3. The main protection was offered by corrosion products, this effect was more significant in the presence of a full coverage FeCO3 layer. FeCO3-rich layer not only prevented the embedment of silty sand but also reduced the adsorption. Silty sand and corrosion products layer exhibited an obvious antagonism effect.
引用
收藏
页数：19
相关论文
共 50 条
  • [21] Interaction of inhibitors with corrosion scale formed on N80 steel in CO2-saturated NaCl solution
    Liu, D.
    Qiu, Y. B.
    Tomoe, Y.
    Bando, K.
    Guo, X. P.
    MATERIALS AND CORROSION-WERKSTOFFE UND KORROSION, 2011, 62 (12): : 1153 - 1158
  • [22] Corrosion Behavior of N80 Steel in Underground Supercritical CO2 Environments
    Ma, Guoliang
    CHEMISTRY AND TECHNOLOGY OF FUELS AND OILS, 2024, 60 (02) : 491 - 500
  • [23] The EIS analysis of electrode reactions of CO2 corrosion of N80 steel
    Chen, CF
    Lu, MX
    Zhao, GX
    Bai, ZQ
    Yan, ML
    Yang, YQ
    ACTA METALLURGICA SINICA, 2002, 38 (07) : 770 - 774
  • [24] Effect of silty sand on the pre-passivation behaviour of 1Cr steel in a CO2 aqueous environment
    Zhao, Yonggang
    Liu, Wei
    Banthukul, Wongpat
    Fan, Yueming
    Li, Xiaogang
    CORROSION ENGINEERING SCIENCE AND TECHNOLOGY, 2020, 55 (03) : 205 - 216
  • [25] Corrosion and protection studies of N80 steel in CO2 solution
    Huang, Xianqiu
    Zheng, Jiashen
    He, Rui
    Liu, Jianrong
    Bai, Huiping
    Tu, Yuanqiang
    MATERIALS AND MANUFACTURING, PTS 1 AND 2, 2011, 299-300 : 34 - +
  • [26] Electrochemical behaviour of N80 steel in CO2 environment at high temperature and pressure conditions
    Ren, Xiedong
    Wang, Hu
    Wei, Qiang
    Lu, Yuan
    Xiao, Bowen
    Xie, Juan
    CORROSION SCIENCE, 2021, 189
  • [27] The EIS analysis of cathodic reactions during CO2 corrosion of N80 steel
    Chen, CF
    Lu, MX
    Zhao, GX
    Bai, ZQ
    Yan, ML
    Yang, YQ
    ACTA METALLURGICA SINICA, 2003, 39 (01) : 94 - 98
  • [28] Mechanical properties of Co2 corrosion scale on N80 well tube steel
    Chen, CF
    Lu, MX
    Zhao, GX
    Bai, ZQ
    Yan, ML
    Yang, YQ
    ACTA METALLURGICA SINICA, 2003, 39 (02) : 175 - 181
  • [29] Corrosion behaviour of N80 carbon steel in formation water under dynamic supercritical CO2 condition
    Zhang, G. A.
    Liu, D.
    Li, Y. Z.
    Guo, X. P.
    CORROSION SCIENCE, 2017, 120 : 107 - 120
  • [30] Inhibition of CO2 corrosion of N80 carbon steel by carboxylic quaternary imidazoline and halide ions additives
    P. C. Okafor
    C. B. Liu
    X. Liu
    Y. G. Zheng
    Journal of Applied Electrochemistry, 2009, 39 : 2535 - 2543
12345