Effect of different solute additions on dendrite morphology and orientation selection in cast binary magnesium alloys

被引:71
作者
Yang, M. [1 ]
Xiong, S-M [1 ,2 ]
Guo, Z. [1 ]
机构
[1] Tsinghua Univ, Sch Mat Sci & Engn, Beijing 100084, Peoples R China
[2] Minist Educ, Key Lab Adv Mat Proc Technol, Beijing, Peoples R China
基金
中国国家自然科学基金;
关键词
Dendrite; Magnesium alloys; X-ray tomography; Phase field simulation; GROWTH DIRECTIONS; ZN ALLOYS; SOLIDIFICATION; EVOLUTION; METALS; SIMULATION; COATINGS; TEXTURE; SURFACE;
D O I
10.1016/j.actamat.2016.04.014
中图分类号
T [工业技术];
学科分类号
08 ;
摘要
In solidification, dendritic morphology was observed to change accordingly if either the type or quantity of the additional element was modified. To gain insight into this phenomenon, the 3D dendrite morphology of different binary magnesium alloys, including MgAl, MgBa, MgCa and MgZn alloys was characterized using synchrotron X-ray tomography and electron backscattered diffraction. Results showed that for most Mg -based alloys, the dendrite exhibited a typical 18 -branch morphology with preferred growth orientations along < 11 (2) over bar0 > and < 11 (2) over bar3 >, whereas for MgZn alloys, the dendrite morphology would change from the 18 -branch pattern to 12 -branch if the Zn content increased, i.e. the so-called dendrite orientation transition (DOT) took place. This DOT behaviour of the Mg alloy dendrite was then successfully modelled using the 3D phase field method by changing the magnitude of related parameters in the specially formulated anisotropy function based on spherical harmonics. (C) 2016 Acta Materialia Inc. Published by Elsevier Ltd. All rights reserved.
引用
收藏
页码:261 / 272
页数:12
相关论文
共 37 条
[1]  
[Anonymous], 1998, FUNDAMENTALS SOLIDIF
[2]   Solidification microstructures and solid-state parallels: Recent developments, future directions [J].
Asta, M. ;
Beckermann, C. ;
Karma, A. ;
Kurz, W. ;
Napolitano, R. ;
Plapp, M. ;
Purdy, G. ;
Rappaz, M. ;
Trivedi, R. .
ACTA MATERIALIA, 2009, 57 (04) :941-971
[3]   DENDRITIC MORPHOLOGY IN ZN-CD DILUTE ALLOYS [J].
AUDERO, MA ;
BILONI, H .
JOURNAL OF CRYSTAL GROWTH, 1972, 12 (04) :297-&
[4]  
Chadwick G.A., 1967, MET SCI J, V1, P132, DOI DOI 10.1179/MSC.1967.1.1.132
[5]   Phase-field models for microstructure evolution [J].
Chen, LQ .
ANNUAL REVIEW OF MATERIALS RESEARCH, 2002, 32 :113-140
[6]   Tip-splitting instability and transition to seaweed growth during alloy solidification in anisotropically preferred growth direction [J].
Chen, Yun ;
Billia, Bernard ;
Li, Dian Zhong ;
Nguyen-Thi, Henri ;
Xiao, Na Min ;
Bogno, Abdoul-Aziz .
ACTA MATERIALIA, 2014, 66 :219-231
[7]   Dendritic Growth Morphologies in Al-Zn Alloys-Part II: Phase-Field Computations [J].
Dantzig, J. A. ;
Di Napoli, Paolo ;
Friedli, J. ;
Rappaz, M. .
METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 2013, 44A (12) :5532-5543
[8]  
Dantzig J. A., 2009, SOLIDIFICATION
[9]  
Dean J.A., 2001, Lange's Handbook of Chemistry, V15
[10]   Phase-field simulation of microstructure formation in technical magnesium alloys [J].
Eiken, Janin .
INTERNATIONAL JOURNAL OF MATERIALS RESEARCH, 2010, 101 (04) :503-509