Fracture toughness of borides formed on boronized ductile iron

被引：47
作者：
Sen, U
Sen, S
Koksal, S
Yilmaz, F
机构：
[1] Sakarya Univ, Dept Met Educ, Tech Educ Fac, TR-54187 Sakarya, Turkey
[2] Sakarya Univ, Dept Met & Mat Engn, Fac Engn, TR-54187 Sakarya, Turkey
来源：
MATERIALS & DESIGN | 2005年 / 26卷 / 02期
关键词：
boronizing; ductile irons; hardness; fracture toughness;
D O I：
10.1016/j.matdes.2004.05.015
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
In this study, fracture toughness properties of boronized ductile iron were investigated. Boronizing was realized in a salt bath consisting of borax, boric acid and ferro-silicon. Boronizing heat treatment was carried out between 850 and 950 degreesC under the atmospheric pressure for 2-8 h. Borides e.g. FeB, Fe,13 formed on ductile iron was verified by X-ray diffraction (XRD) analysis, SEM and optical microscope. Experimental results revealed that longer boronizing time resulted in thicker boride layers. Optical microscope cross-sectional observation of borided layers showed dentricular morphology. Both microhardness and fracture toughness of borided surfaces were measured via Vickers indenter. The harnesses of borides formed on the ductile iron were in the range of 1160-2140 HV0.1 and fracture toughness were in the range of 2.19-4.47 MPa m(1/2) depending on boronizing time and temperature. (C) 2004 Elsevier Ltd. All rights reserved.
引用
收藏
页码：175 / 179
页数：5
相关论文
共 50 条
  • [41] Effect of boronizing composition on boride layer of boronized GGG-60 ductile cast iron
    Kul, M.
    Oskay, K. O.
    TemizkanA, A.
    Karaca, B.
    Kumruoglu, L. C.
    Topcu, B.
    VACUUM, 2016, 126 : 80 - 83
  • [42] Fracture toughness of superplastic formed/diffusion bonded interfaces
    Xiang, Y
    Wu, S
    Chen, D
    JOURNAL OF MATERIALS ENGINEERING AND PERFORMANCE, 2001, 10 (06) : 679 - 684
  • [43] Fracture toughness of superplastic formed/diffusion bonded interfaces
    Y. Xiang
    S. Wu
    D. Chen
    Journal of Materials Engineering and Performance, 2001, 10 : 679 - 684
  • [44] Predicting the effect of constraint on cleavage and ductile fracture toughness using area contour toughness scaling
    Seal, C. K.
    Sherry, A. H.
    ENGINEERING FRACTURE MECHANICS, 2017, 186 : 347 - 367
  • [45] Effects of Ductile Fiber Size on the Fracture Toughness of Copper/Polyester Composites
    Kaman, Mete Onur
    Solmaz, Murat Yavuz
    Turan, Kadir
    JOURNAL OF COMPOSITE MATERIALS, 2010, 44 (26) : 3151 - 3164
  • [46] Mechanical behavior of borides formed on borided cold work tool steel
    Sen, S
    Ozbek, I
    Sen, U
    Bindal, C
    SURFACE & COATINGS TECHNOLOGY, 2001, 135 (2-3) : 173 - 177
  • [47] Reconciling fracture toughness parameter contradictions in thin ductile metal sheets
    Lanning, W. R.
    Javaid, S. S.
    Muhlstein, C. L.
    FATIGUE & FRACTURE OF ENGINEERING MATERIALS & STRUCTURES, 2017, 40 (11) : 1809 - 1824
  • [48] Effect of competing mechanisms on fracture toughness of metals with ductile grain structures
    Li, Yan
    Zhou, Min
    ENGINEERING FRACTURE MECHANICS, 2019, 205 : 14 - 27
  • [49] On the temperature dependence of fracture toughness in the brittle-to-ductile transition region
    A. A. Kaminskii
    G. V. Galatenko
    International Applied Mechanics, 1999, 35 : 398 - 404
  • [50] Controlling fracture toughness of matrix for ductile fiber reinforced cementitious composites
    Kawamata, A
    Mihashi, H
    Kaneko, Y
    Kirikoshi, K
    ENGINEERING FRACTURE MECHANICS, 2002, 69 (02) : 249 - 265
12345