Precipitates evolution of the AA7075-H18 alloy sheet during the application of the solution heat treatment process

被引：7

作者：

Wang, Gang ^{[1
]}

Gu, Zhengwei ^{[1
]}

Yu, Ge ^{[1
]}

Li, Xin ^{[1
]}

机构：

[1] Jilin Univ, Coll Mat Sci & Engn, Key Lab Automobile Mat, Changchun 130022, Peoples R China

来源：

MATERIALS LETTERS | 2022年 / 318卷

关键词：

Metals and alloys; Microstructure; Phase transformation; Solution treatment; MECHANICAL-PROPERTIES; ZN; PARTICLES;

D O I：

10.1016/j.matlet.2022.132230

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

The hot stamping technology of the high-strength aluminum alloy sheet has attracted increased attention from both the scientific community and industry due to the rapidly growing demand for lightweight automobiles. However, the development of a proper solution process suitable for the hot stamping technique remains a great challenge. Along these lines, in this work, the precipitates evolution of the AA7075-H18 alloy sheet with a thickness of 2 mm during the implementation of the solution process was systematically studied. The insoluble particles (i.e., Al23CuFe4 and Mg2Si) and the soluble particles (eta-MgZn2) were clearly identified from the aluminum matrix. Moreover, the transformation sequence during the solution heat treatment was determined, and a reasonable solution temperature window was also established.

引用

页数：3

共 24 条

[21] Microstructure Evolution during Solution Treatment Cooling Process of BT22 Alloy Large-Sized Forged Rods
Wu Xiaodong
Ge Peng
Xi Zhengping
Mao Xiaonan
Yang Guanjun
Zhou Wei
RARE METAL MATERIALS AND ENGINEERING, 2010, 39 (09) : 1555 - 1560
[22] Application of novel physical picture based on artificial neural networks to predict microstructure evolution of Al-Zn-Mg-Cu alloy during solid solution process
Liu, Jiao-jiao
Li, Hong-ying
Li, De-wang
Wu, Yue
TRANSACTIONS OF NONFERROUS METALS SOCIETY OF CHINA, 2015, 25 (03) : 944 - 953
[23] Evolution of the second phase particles during the heating-up process of solution treatment of Al-Zn-Mg-Cu alloy
Peng, Guosheng
Chen, Kanghua
Chen, Songyi
Fang, Huachan
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2015, 641 : 237 - 241
[24] Effects of additive manufacturing process parameters and heat treatment on texture evolution and variant selection during austenite-martensite transformation in 18%Ni-M350 maraging steel
Truong, T. D.
Asala, G.
Ola, O. T.
Ojo, O. A.
Odeshi, A. G.
MATERIALS CHARACTERIZATION, 2023, 204

← 1 2 3 →