Self-assembly and crystallization behavior of a double-crystalline polyethylene-block-poly(ethylene oxide) diblock copolymer

The self-assembly and crystallization behavior of a well-defined low molecular weight polyethylene-block-poly(ethylene oxide) (PE-b-PEO) diblock copolymer was studied. The number-average degrees of polymerization for the PE and PEO blocks were 29 and 20, respectively. The molecular weight distribution was 1.04 as determined by size-exclusion chromatography. The PE-b-PEO sample exhibited two melting points at 28.7 and 97.4 degreesC for the PEO and the PE crystals, respectively. The crystallization of the PE blocks was unconfined, while the crystallization of the PEO blocks was confined between pre-existing PE crystalline lamellae, as demonstrated by simultaneous small-angle X-ray scattering (SAXS) and wide-angle X-ray diffraction (WAXD) studies. In the fully crystalline state, both PE and PEO blocks formed extended-chain crystals with PE chains tilted similar to 22degrees from the lamellar normal and PEO chains parallel to the lamellar normal, as evidenced by two-dimensional WAXD study of shear-oriented samples. Regardless of hydrogen bonding among hydroxyl chain ends in the PEO blocks, interdigitated, single-crystalline layer morphology was observed for both PE and PEO crystals. The partial crystalline morphology, where the PE crystallizes and the PEO is amorphous, had the same overall d-spacing as the fully crystalline morphology. A double-amorphous PEO layer sandwiched between neighboring PE crystalline layers was deduced based on a chain conformation study using Fourier transform infrared. The confined crystallization kinetics for PEO blocks was investigated by differential scanning calorimetry, which could be explained by a heterogeneous nucleation mechanism. The slower crystallization rate in the PEO-block than the same molecular weight homopolymer was attributed to the effects of nanoconfinement and PEO chains tethered to the PE crystals. (C) 2004 Elsevier Ltd. All rights reserved.