Recrystallization of tensile-deformed Fe-11Cr-19Ni alloy single crystal

被引:1
作者
Okada, T [1 ]
Takechi, K [1 ]
Noda, H [1 ]
Liu, WY [1 ]
Tagami, M [1 ]
Inoko, F [1 ]
机构
[1] Univ Tokushima, Dept Mech Engn, Tokushima 7708506, Japan
来源
MATERIALS TRANSACTIONS JIM | 2000年 / 41卷 / 08期
关键词
iron-11% chromium-19% nickel alloy; single crystal; tensile deformation; recrystallization; < 111 >-rotation;
D O I
10.2320/matertrans1989.41.1082
中图分类号
T [工业技术];
学科分类号
08 ;
摘要
An Fe-11Cr-19Ni alloy single crystal was deformed in tension along a direction close to [011] to a strain of 0.31 at room temperature. Deformation was uniform both macroscopically and microscopically, without the formation of deformation bands. The crystal was rotated such that the primary slip direction moved towards the tensile direction. After annealing, small recrystallized grains were formed. They were separated from each other. The orientations of about half of the recrystallized grains were described by the orientation of the deformed matrix rotated about [111] axes. The recrystallized grains with orientations rotated about the conjugate-slip plane normal and the cross-slip plane normal were predominant. The rotating direction was opposite to the matrix rotation during tensile deformation.
引用
收藏
页码:1082 / 1087
页数:6
相关论文
共 14 条
[1]   Block models and (011)[100]recrystallized orientation in cold rolled single crystals of αiron -: A critical review [J].
Furubayashi, E .
ISIJ INTERNATIONAL, 1998, 38 (06) :510-517
[2]  
FURUBAYASHI EI, 1969, T IRON STEEL I JPN, V9, P222
[3]  
INOKO F, 1993, MATERIALS SCI FORUM, V113, P139
[4]   Recrystallization behavior at deformation bands in <011>aluminum single crystals [J].
Kashihara, K ;
Tagami, M ;
Inoko, F .
MATERIALS TRANSACTIONS JIM, 1996, 37 (04) :572-578
[5]   Deformed structure and crystal orientation at deformation bands in <011>aluminum single crystals [J].
Kashihara, K ;
Tagami, M ;
Inoko, F .
MATERIALS TRANSACTIONS JIM, 1996, 37 (04) :564-571
[6]  
KASHIHARA K, IN PRESS MAT SCI E A
[7]  
KASHIHARA K, 1997, P THERMEC 97, P1075
[8]  
KASHIHARA K, 1998, P 6 INT C AL ALL ICA, P1143
[9]   Recrystallization involving (111) rotation in Fe-11Cr-19Ni alloy single crystal [J].
Okada, T ;
Takechi, K ;
Takenaka, U ;
Liu, WY ;
Tagami, M ;
Inoko, F .
MATERIALS TRANSACTIONS JIM, 2000, 41 (04) :470-475
[10]  
OKADA T, IN PRESS