The Effects of Molding Materials on Microstructure and Wear Behavior of A356 Alloy

被引：4
|
作者：
Yildirim, Musa [1 ]
Ozyurek, Dursun [1 ]
Tuncay, Tansel [1 ]
机构：
[1] Karabuk Univ, Technol Fac, Dept Mfg Engn, Karabuk, Turkey
来源：
HIGH TEMPERATURE MATERIALS AND PROCESSES | 2017年 / 36卷 / 05期
关键词：
A356; cooling rate; wear behavior; SI-MG ALLOYS; MECHANICAL-PROPERTIES; SLIDING WEAR; HEAT-TREATMENT; CU; TEMPERATURE; ALUMINUM; FE;
D O I：
10.1515/htmp-2015-0240
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
In this study, the effect of molding materials on microstructure and wear behavior of A356 alloy was investigated. Different microstructures were obtained by casting A356 alloy into the molds made from three different materials. Homogenization and aging heat treatments were applied as cast blocks. The aged samples were tested by pin-on-disk-type standard wear equipment. The results showed that casting into different mold materials resulted in different microstructures of A356 alloy. Microstructures of the Al-Si-Mg alloy differ depending on the mold materials. Secondary dendrite arm space (SDAS) decreased proportionally with increasing cooling rate. Based on the cooling rate, hardness values of the alloy also differ. As the cooling rate increased, hardness of the alloy increased. The SDAS increased due to the decreasing cooling rate. In wear tests, increasing weight loss was observed with decreasing cooling rate.
引用
收藏
页码：515 / 521
页数：7
相关论文
共 50 条
  • [21] Effects of rheocasting and heat treatment on microstructure and mechanical properties of A356 alloy
    Liao BoChao
    YoungKoo, Park
    Ding HongSheng
    MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2011, 528 (03): : 986 - 995
  • [22] The Effects of Cr and Zr Additives on the Microstructure and Mechanical Properties of A356 Alloy
    Tuncay, Tansel
    Ozyurek, Dursun
    Dispinar, Derya
    Tekeli, Suleyman
    TRANSACTIONS OF THE INDIAN INSTITUTE OF METALS, 2020, 73 (05) : 1273 - 1285
  • [23] The Effects of Cr and Zr Additives on the Microstructure and Mechanical Properties of A356 Alloy
    Tansel Tunçay
    Dursun Özyürek
    Derya Dişpinar
    Süleyman Tekeli
    Transactions of the Indian Institute of Metals, 2020, 73 : 1273 - 1285
  • [24] Effect of a novel thixoforming process on the microstructure and fracture behavior of A356 aluminum alloy
    Boostani, A. Fadavi
    Tahamtan, S.
    MATERIALS & DESIGN, 2010, 31 (08) : 3769 - 3776
  • [25] Experimental study of the effect of wear parameters on the wear behavior of A356 alloy/cow horn particulate composites
    B.Q.Ochieze
    C.C.Nwobi-Okoye
    P.N.Atamuo
    Defence Technology, 2018, (01) : 77 - 82
  • [26] Experimental study of the effect of wear parameters on the wear behavior of A356 alloy/cow horn particulate composites
    Ochieze, B. Q.
    Nwobi-Okoye, C. C.
    Atamuo, P. N.
    DEFENCE TECHNOLOGY, 2018, 14 (01): : 77 - 82
  • [27] Experimental study of the effect of wear parameters on the wear behavior of A356 alloy/cow horn particulate composites
    BQOchieze
    CCNwobiOkoye
    PNAtamuo
    Defence Technology, 2018, 14 (01) : 77 - 82
  • [28] Microstructure evolution of A356 alloy in a novel rheocasting approach
    Zhang Xiao-li
    Li Ting-ju
    Xie Shui-sheng
    Teng Hai-Tao
    Jin Jun-ze
    JOURNAL OF MATERIALS PROCESSING TECHNOLOGY, 2009, 209 (04) : 2092 - 2098
  • [29] Microstructure evolution of A356 alloy under compound field
    Zhang, Zhongtao
    Li, Jie
    Yue, Hongyun
    Zhang, Jian
    Li, Tingju
    JOURNAL OF ALLOYS AND COMPOUNDS, 2009, 484 (1-2) : 458 - 462
  • [30] Effect of Ti content on microstructure and hardness of A356 alloy
    Qu, Min
    Zheng, Liubin
    Zhao, Ming
    Li, Tingting
    Liu, Fengbin
    He, Guangping
    ADVANCED ENGINEERING MATERIALS II, PTS 1-3, 2012, 535-537 : 932 - 935
12345