INFLUENCE OF STRUCTURAL STATE ON CAVITATIONAL EROSION OF AUSTENITIC STAINLESS STEEL SOLUTION TREATMENT AND NITRIDING

被引：0
|
作者：
Padurean, Ioan [1 ]
Ionel, Ioana [1 ]
机构：
[1] Politehn Univ Timisoara, Mecan Fac, Timisoara, Romania
来源：
METALURGIA INTERNATIONAL | 2010年 / 15卷 / 10期
关键词：
cavitation erosion; nitriding; structural analyses; thermal treatment; microstructure;
D O I：
暂无
中图分类号：
TF [冶金工业];
学科分类号：
0806 ;
摘要：
Samples of the austenitic stainless steel GX5CrNi19-10 have been thermally treated by solution treatment followed by nitriding After that treatment the samples of that stainless steel was tested at cavitation erosion In the areas affected by cavitation appear structure changes, micro cracks in a structure, separation and expulsions in structure Were obtained cavitation erosion resistance increases due to structural changes There were hardness and microstructure analysis Showed how steel structure influence on mass loss by cavitation. In conclusion, the thermal treatment of solution treatment followed by nitriding give a high cavitational erosion resistance to austenitic stainless steel GX5CrNi19-10.
引用
收藏
页码：55 / 59
页数：5
相关论文
共 50 条
  • [21] Active screen plasma nitriding of austenitic stainless steel
    Li, CX
    Georges, J
    Li, XY
    SURFACE ENGINEERING, 2002, 18 (06) : 453 - 458
  • [22] Low Temperature Plasma Nitriding Of Austenitic Stainless Steel
    Istiroyah
    Santjojo, D. J.
    DISRUPTIVE INNOVATION IN MECHANICAL ENGINEERING FOR INDUSTRY COMPETITIVENESS, 2018, 1983
  • [23] Activated solution nitriding of stainless steel
    Spies, HJ
    Berg, HJ
    Vogt, F
    Serchen, B
    ADVANCED ENGINEERING MATERIALS, 2000, 2 (1-2) : 38 - 39
  • [24] Glow-discharge nitriding of AISI 316L austenitic stainless steel: influence of treatment temperature
    Borgioli, F
    Fossati, A
    Galvanetto, E
    Bacci, T
    SURFACE & COATINGS TECHNOLOGY, 2005, 200 (07): : 2474 - 2480
  • [25] Glow-discharge nitriding of AISI 316L austenitic stainless steel: influence of treatment time
    Fossati, A
    Borgioli, F
    Galvanetto, E
    Bacci, T
    SURFACE & COATINGS TECHNOLOGY, 2006, 200 (11): : 3511 - 3517
  • [26] Glow-discharge nitriding of ISO 5832-1 austenitic stainless steel: Influence of treatment time
    Dos Reis, R. F.
    Maliska, A. M.
    Borges, P. C.
    MATERIA-RIO DE JANEIRO, 2008, 13 (02): : 304 - 315
  • [27] Influence of time on the microstructure of AISI 321 austenitic stainless steel in salt bath nitriding
    Wang, Jun
    Lin, Yuanhua
    Yan, Jing
    Zen, Dezhi
    Zhang, Qiang
    Huang, Runbo
    Fan, Hongyuan
    SURFACE & COATINGS TECHNOLOGY, 2012, 206 (15): : 3399 - 3404
  • [28] Mechanisms of the Hydrogen Influence on the Diffusivity of Nitrogen During Plasma Nitriding Austenitic Stainless Steel
    Moskalioviene, Teresa
    Galdikas, Arvaidas
    METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 2019, 50A (02): : 1021 - 1032
  • [29] Improvement of the slurry erosion resistance of an austenitic stainless steel with combinations of surface treatments:: Nitriding and TiN coating
    Recco, Abel Andre C.
    Lopez, Diana
    Bevilacqua, Andre F.
    da Silva, Felipe
    Tschiptschin, Andre P.
    SURFACE & COATINGS TECHNOLOGY, 2007, 202 (4-7): : 993 - 997
  • [30] Mechanisms of the Hydrogen Influence on the Diffusivity of Nitrogen During Plasma Nitriding Austenitic Stainless Steel
    Teresa Moskalioviene
    Arvaidas Galdikas
    Metallurgical and Materials Transactions A, 2019, 50 : 1021 - 1032
12345