Failure modes in plasma-sprayed thermal barrier coatings

被引:383
作者
Schlichting, KW
Padture, NP [1 ]
Jordan, EH
Gell, M
机构
[1] Univ Connecticut, Dept Mat & Met Engn, Inst Mat Sci, Storrs, CT 06269 USA
[2] Univ Connecticut, Inst Mat Sci, Dept Mech Engn, Storrs, CT 06269 USA
来源
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING | 2003年 / 342卷 / 1-2期
关键词
thermal barrier coatings; plasma spray; thermo-mechanical fatigue; ceramics;
D O I
10.1016/S0921-5093(02)00251-4
中图分类号
TB3 [工程材料学];
学科分类号
0805 ; 080502 ;
摘要
Commercial plasma-sprayed thermal barrier coatings (TBCs) were investigated in an effort to elucidate the failure modes during thermal-cycling. Residual stresses in the thermally grown oxide (TGO) was measured using the Cr3+ photoluminescence piezo-spectroscopy (PLPS) method and the microstructures of the TBCs were characterized as a function of thermal cycles. The average residual stress in the TGO was found to be of the order of 1 GPa. The average thermal-cyclic life of the TBCs was found to be similar to 350 cycles. Microstructural observations revealed that as the TGO thickened, cracking occurred at the bond-coat/TGO interface, and in some instances cracking also occurred at the TGO/top-coat interface, but primarily at crests of bond-coat undulations. The bondcoat-TGO separation resulted in 'layering' of the TGO at crests due to enhanced TGO thickening in those regions. In the troughs of bond-coat undulations, cracking occurred within the top-coat when the TGO was thick. Thus, the primary failure modes in these TBCs were: (i) cracking of the bond-coat/TGO interface; (ii) cracking within the top-coat; and (iii) linking of these microcracks by fracture of the TGO. A semi-quantitative failure model has been used to rationalize some of the observed cracking modes. Based on this analysis some suggestions are made for improving TBC durability. (C) 2002 Elsevier Science B.V. All rights reserved.
引用
收藏
页码:120 / 130
页数:11
相关论文
共 36 条
[1]  
[Anonymous], 1996, Metallurgical and Ceramic Protective Coatings
[2]  
BEARDSLEY MB, 1990, P 1990 COAT ADV HEAT, P1153
[3]   CRACKING OF THIN BONDED FILMS IN RESIDUAL TENSION [J].
BEUTH, JL .
INTERNATIONAL JOURNAL OF SOLIDS AND STRUCTURES, 1992, 29 (13) :1657-1675
[4]   Nondestructive evaluation of the oxidation stresses through thermal barrier coatings using Cr3+ piezospectroscopy [J].
Christensen, RJ ;
Lipkin, DM ;
Clarke, DR ;
Murphy, K .
APPLIED PHYSICS LETTERS, 1996, 69 (24) :3754-3756
[5]  
CHRISTENSEN RM, 1979, MECH COMPOSITE MAT, P47
[6]   Critical radius for interface separation of a compressively stressed film from a rough surface [J].
Clarke, DR ;
Pompe, W .
ACTA MATERIALIA, 1999, 47 (06) :1749-1756
[7]   STRESSES IN BONDED MATERIALS WITH A CRACK PERPENDICULAR TO INTERFACE [J].
COOK, TS ;
ERDOGAN, F .
INTERNATIONAL JOURNAL OF ENGINEERING SCIENCE, 1972, 10 (08) :677-+
[8]  
DAVIDGE RW, 1979, MECH BEHAV CERAMICS, P85
[9]  
DEMASI JT, 1989, 182230 NASA
[10]   Mechanisms controlling the durability of thermal barrier coatings [J].
Evans, AG ;
Mumm, DR ;
Hutchinson, JW ;
Meier, GH ;
Pettit, FS .
PROGRESS IN MATERIALS SCIENCE, 2001, 46 (05) :505-553