Effects of low-temperature duplex coatings on corrosion behavior of austempered ductile iron

被引：7
作者：
Hsu, Cheng-Hsun [1 ]
Chen, Kai-Lin [1 ]
Lee, Chun-Ying [1 ]
Lu, Kuan-Chain [1 ]
机构：
[1] Tatung Univ, Dept Mat Engn, Taipei 10451, Taiwan
来源：
SURFACE & COATINGS TECHNOLOGY | 2009年 / 204卷 / 6-7期
关键词：
Electroless nickel; Cathodic arc evaporation; ADI; CrTiAlN; Corrosion resistance; RESISTANCE;
D O I：
10.1016/j.surfcoat.2009.04.002
中图分类号：
TB3 [工程材料学];
学科分类号：
0805 ; 080502 ;
摘要：
This study utilized electroless nickel (EN) and cathodic arc evaporation (CAE) technologies, with the known advantage of low processing temperature (EN = 90 degrees C and CAE = 230 degrees C), to treat the austempered ductile iron (ADI) substrate. The eligibility of applying the EN and CAE-CrTiAlN duplex coatings on ADI, along with the coating properties, such as structure, roughness, and adhesion, were evaluated and analyzed. Moreover, polarization and immersion tests were performed to further understand the effects of the coatings on the corrosion resistance of ADI. The results showed that the unique microstructure of ADI did not deteriorate after EN and CAE treatments. With regard to corrosion resistance, the duplex coated specimens performed better than did the uncoated and monolithic EN or CrTiAlN coated ones in 3.5 wt.% NaCl and 10 vol.% H(2)SO(4) aqueous solutions. (C) 2009 Elsevier B.V. All rights reserved.
引用
收藏
页码：997 / 1001
页数：5
相关论文
共 50 条
  • [31] Effect of austenitization temperature on microstructure and mechanical properties of low-carbon-equivalent carbidic austempered ductile iron
    Dakre, Vinayak
    Peshwe, D. R.
    Pathak, S. U.
    Likhite, Ajay
    INTERNATIONAL JOURNAL OF MINERALS METALLURGY AND MATERIALS, 2018, 25 (07) : 770 - 778
  • [32] Effect of austempering temperature and manganese content on the impact energy of austempered ductile iron
    Hegde, Ananda
    Gurumurthy, B. M.
    Hindi, Jamaluddin
    Sharma, Sathyashankara
    Gowrishankar, M. C.
    COGENT ENGINEERING, 2021, 8 (01):
  • [33] Corrosion behaviors of low-temperature plasma nickelized coatings on titanium alloy
    Fu, T. -L.
    Zhan, Z. -L.
    Zhang, L.
    Yang, Y. -R.
    Liu, Z.
    Liu, J. -X.
    MATERIALS AND CORROSION-WERKSTOFFE UND KORROSION, 2016, 67 (12): : 1321 - 1328
  • [34] Artificial Neural Networks for Producing a Low-Cost Austempered Ductile Iron
    Hofmam, Diogo
    Ramos, Fabiano Dornelles
    Lemos, Guilherme Vieira Braga
    de Lima Lessa, Cleber Rodrigo
    MATERIALS RESEARCH-IBERO-AMERICAN JOURNAL OF MATERIALS, 2022, 25
  • [35] TEMPERED MICROSTRUCTURE AND MECHANICAL PROPERTIES OF AUSTEMPERED LOW ALLOYED BAINITIC DUCTILE IRON
    Cui Junjun
    Chen Liqing
    Li Haizhi
    Tong Weiping
    ACTA METALLURGICA SINICA, 2016, 52 (07) : 778 - 786
  • [36] Corrosion behaviour and structure of the surface layer formed on austempered ductile iron in concentrated sulphuric acid
    Krawiec, H
    Stypula, B
    Stoch, J
    Mikolajczyk, M
    CORROSION SCIENCE, 2006, 48 (03) : 595 - 607
  • [37] Effects of austempering temperature on microstructure and surface residual stress of carbidic austempered ductile iron (CADI) grinding balls
    Liu, Jin-hai
    Xiong, Peng
    Fu, Bin-guo
    Yang, Wei-ting
    Zhao, Xue-bo
    Han, Zi-ang
    Li, Guo-lu
    CHINA FOUNDRY, 2018, 15 (03) : 173 - 180
  • [38] Micromechanical modelling of constitutive behavior of austempered ductile iron (ADI) at high strain rate
    Iannitti, G.
    Ruggiero, A.
    Bonora, N.
    Masaggia, S.
    Veneri, F.
    THEORETICAL AND APPLIED FRACTURE MECHANICS, 2017, 92 : 351 - 359
  • [39] Corrosion behavior of boro-tempered ductile iron
    Kayali, Y.
    Buyuksagis, A.
    Yalcin, Y.
    PROTECTION OF METALS AND PHYSICAL CHEMISTRY OF SURFACES, 2010, 46 (03) : 345 - 349
  • [40] Effects of graphite nodule count on microstructural homogeneity of austempered ductile iron (ADI)
    Hu, Zhitao
    Wang, Xin
    Du, Yuzhou
    Liu, Chen
    Gao, Zhijie
    Li, Jiaze
    Jiang, Bailing
    METALLURGICAL RESEARCH & TECHNOLOGY, 2023, 120 (02)
12345