Lithium aluminum manganese oxide having spinel-framework structure for long-life lithium-ion batteries

被引:57
作者
Ariyoshi, Kingo [1 ]
Iwata, Eiichi
Kuniyoshi, Minoru
Wakabayashi, Hiromichi
Ohzuku, Tsutomu
机构
[1] Osaka City Univ, Grad Sch Engn, Dept Appl Chem, Osaka 5588585, Japan
[2] Tosoh Corp, Proc Dev, Nanyo Technol Ctr, Yamaguchi 7468501, Japan
关键词
D O I
10.1149/1.2360019
中图分类号
O646 [电化学、电解、磁化学];
学科分类号
081704 ;
摘要
Lithium aluminum manganese oxide (LAMO) having a spinel-framework structure (a=8.211 A) was prepared and examined in lithium nonaqueous cells. LAMO shows extremely small irreversible capacity with rechargeable capacity of ca. 105 mAh g(-1) in lithium cells operated in voltage of 3 to 5 V. To show durability for long-life applications, a 2.5 V lithium-ion cell of Li[Li1/3Ti5/3]O-4 and LAMO was fabricated and accelerated cycle tests were done at room temperature in voltage of 2 to 3 V for 3600 cycles, and an empirical relation between capacity (Q) and number of cycle (n) was obtained to be Q=102.7-0.144 n(1/2). (c) 2006 The Electrochemical Society.
引用
收藏
页码:A557 / A560
页数:4
相关论文
共 29 条
[1]   Optimization of insertion compounds such as LiMn2O4 for Li-ion batteries [J].
Amatucci, G ;
Tarascon, JM .
JOURNAL OF THE ELECTROCHEMICAL SOCIETY, 2002, 149 (12) :K31-K46
[2]   The elevated temperature performance of the LiMn2O4/C system:: failure and solutions [J].
Amatucci, G ;
Du Pasquier, A ;
Blyr, A ;
Zheng, T ;
Tarascon, JM .
ELECTROCHIMICA ACTA, 1999, 45 (1-2) :255-271
[3]   An asymmetric hybrid nonaqueous energy storage cell [J].
Amatucci, GG ;
Badway, F ;
Du Pasquier, A ;
Zheng, T .
JOURNAL OF THE ELECTROCHEMICAL SOCIETY, 2001, 148 (08) :A930-A939
[4]   Failure mechanism and improvement of the elevated temperature cycling of LiMn2O4 compounds through the use of the LiAlxMn2-xO4-zFz solid solution [J].
Amatucci, GG ;
Pereira, N ;
Zheng, T ;
Tarascon, JM .
JOURNAL OF THE ELECTROCHEMICAL SOCIETY, 2001, 148 (02) :A171-A182
[5]   STRUCTURE AND ELECTROCHEMISTRY OF THE SPINEL OXIDES LITI2O4 AND LI4/3TI5/3O4 [J].
COLBOW, KM ;
DAHN, JR ;
HAERING, RR .
JOURNAL OF POWER SOURCES, 1989, 26 (3-4) :397-402
[6]   TEM studies:: The key for understanding the origin of the 3.3 V and 4.5 V steps observed in LiMn2O4-based spinels [J].
Dupont, L ;
Hervieu, M ;
Rousse, G ;
Masquelier, C ;
Palacín, MR ;
Chabre, Y ;
Tarascon, JM .
JOURNAL OF SOLID STATE CHEMISTRY, 2000, 155 (02) :394-408
[7]   LiMn2-xCuxO4 spinels (0.1≤x≤0.5):: A new class of 5 V cathode materials for Li batteries -: I.: Electrochemical, structural, and spectroscopic studies [J].
Ein-Eli, Y ;
Howard, WF ;
Lu, SH ;
Mukerjee, S ;
McBreen, J ;
Vaughey, JT ;
Thackeray, MM .
JOURNAL OF THE ELECTROCHEMICAL SOCIETY, 1998, 145 (04) :1238-1244
[8]   SPINEL ANODES FOR LITHIUM-ION BATTERIES [J].
FERG, E ;
GUMMOW, RJ ;
DEKOCK, A ;
THACKERAY, MM .
JOURNAL OF THE ELECTROCHEMICAL SOCIETY, 1994, 141 (11) :L147-L150
[9]   Correlation between the growth of the 3.3 V discharge plateau and capacity fading in Li1+xMn2-xO4 materials [J].
Gao, Y ;
Dahn, JR .
SOLID STATE IONICS, 1996, 84 (1-2) :33-40
[10]   IMPROVED CAPACITY RETENTION IN RECHARGEABLE 4V LITHIUM LITHIUM MANGANESE OXIDE (SPINEL) CELLS [J].
GUMMOW, RJ ;
DEKOCK, A ;
THACKERAY, MM .
SOLID STATE IONICS, 1994, 69 (01) :59-67