Boosting NiO Catalytic Activity by x wt % F-ions and K2O for the Production of Methyl Ethyl Ketone (MEK) via Catalytic Dehydrogenation of 2-Butanol

Herein, the synthesis of pure and modified mesoporous nanocrystalline NiO is reported. The catalyst was modified with different wt % F-ions or K2O and used to produce Methyl ethyl ketone (MEK) as a potential fuel/solvent. XRD analysis of the promoted catalysts confirmed the formation of Ni-metal covered by the host oxide, compared with pure NiO, especially for the promoted catalysts with x wt % F-ions. CO2-TPD results demonstrated the existence of different basic sites over these catalysts with varying strength. The catalytic conversion of sec-butanol (SB) into MEK over the parent NiO catalyst showed 52 % and 76.8 % conversion of SB at 250 and 275 degrees C, respectively, with higher selectivity to MEK >96 %. Among the promoted catalysts, NiO-10 wt % F- and NiO-1 wt % K2O catalysts showed 99 and 95 % conversion, respectively, with retaining the MEK selectivity of >= 96 %. The catalytic activity, of the most active catalysts, was correlated with the presence of Ni/NiO interfaces, different types of basic sites, especially strong basic sites, and the surface area and porosity measurements.